A kind of high boron alloy steel material for roll and preparation method thereof

An alloy steel and high boron technology is applied in the field of high boron alloy steel materials for rolls and their preparation, which can solve problems such as harshness and high requirements, and achieve the effects of light segregation, lower production costs, and reduced inclusion oxides.

Inactive Publication Date: 2016-01-20
马鞍山市方圆材料工程股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Pumps and valves work in various and harsh environments, and have high requirements for materials. At present, there are many kinds of alloy steels used for pumps and valves, and the technology has made great progress, but There are still many problems, such as wear resistance, hardness, antirust performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., which cannot meet the production requirements in many occasions, and further improvement is needed to increase production efficiency. , reduce costs, improve safety, provide guarantee for the development of high-precision technology, and provide impetus for social development, the task is still very arduous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-boron alloy steel material for rolls, which contains chemical element components and mass percentages: carbon 0.8-0.9, tungsten 2.5-3, molybdenum 0.15-0.25, vanadium 0.5-0.8, chromium 2.1-2.4, niobium 0.05- 0.10, cerium 0.06-0.10, praseodymium 0.02-0.05, titanium 0.3-0.5, cobalt 0.1-0.15, nickel 0.3-0.5, B0.5-0.8, P≤0.030, S≤0.030, and the balance is iron.

[0014] The production method of the high boron alloy steel material for the roll is characterized in that:

[0015] (1) Prepare pig iron and scrap iron as the source of iron matrix in a ratio of 1:1.5, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for one-time refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;

[0016] (2) The batch sequence of alloying elements put into the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-boron alloy steel material for a roller. The high-boron alloy steel material contains the following chemical elements in percentage by weight: 0.8-0.9% of carbon, 2.5-3% of tungsten, 0.15-0.25% of molybdenum, 0.5-0.8% of vanadium, 2.1-2.4% of chromium, 0.05-0.10% of niobium, 0.06-0.10% of cerium, 0.02-0.05% of praseodymium, 0.3-0.5% of titanium, 0.1-0.15 of cobalt, 0.3-0.5% of nickel, 0.5-0.8% of B, not more than 0.030% of P, not more than 0.030% of S and the balance of iron. The alloy steel provided by the invention has high hardness and wear resistance, as well as relatively good toughness, high heat intensity and high contact fatigue strength, and can also be used for developing a composite steel roller with high content of W and V, light segregation and good wear resistance, so as to meet the requirements of a hot continuous rolling technology, reduce the roller changing frequency in rolling, greatly improve the operation rate of a rolling machine, reduce the production cost and improve economic benefits.

Description

technical field [0001] The invention relates to the field of metal material preparation, in particular to a high-boron alloy steel material for rolls and a preparation method thereof. Background technique [0002] The working environment of pump valves is diverse and harsh, and the requirements for materials are very high. At present, there are many kinds of alloy steel used in pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance Performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., cannot meet the production requirements in many occasions, and further improvement is needed to improve production efficiency, reduce costs, and improve safety. Guaranteeing and providing impetus for social development are still arduous tasks. Contents of the invention [0003] The object of the present invention is to provide a high boron alloy steel materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/54C22C33/04C21C7/04C21D1/26
Inventor 何玉平陶国斌史承海晏绍斌屠明安
Owner 马鞍山市方圆材料工程股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap