A Metallization Process of Honeycomb Epoxy FRP Antenna

A kind of epoxy glass fiber reinforced plastic and metallization technology, applied in the direction of metal material coating process, liquid chemical plating, coating, etc., can solve the problem of insufficient strength and other problems, achieve strong bonding force, easy production, processing and promotion, bright surface. Effect

Active Publication Date: 2016-08-17
36TH RES INST OF CETC
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above methods are suitable for non-metals with dense structures such as plastics, they are not strong enough, especially for epoxy glass fiber reinforced plastics with honeycomb sandwich structure, this kind of process is not suitable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The metallization process of epoxy FRP antenna with honeycomb sandwich structure refers to the process of obtaining a certain thickness of metal film layer through modification treatment on the surface of epoxy FRP matrix with honeycomb sandwich structure.

[0018] The process route of the present invention can be summarized as: antenna surface sealing modification treatment → antenna pre-treatment (including degreasing roughening and modified sealing material roughening) → antenna metallization treatment (including chemical metal film formation and electroplating thickening) → metal The post-treatment of the three defenses of the film layer is such a sequential process.

[0019] 1. Antenna surface sealing modification treatment

[0020] The sealing modification treatment of the antenna surface refers to: 1) firstly wipe the surface of the honeycomb sandwich structure epoxy glass fiber reinforced plastic substrate to be metallized with alcohol, and then preheat it at 45...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metallization process for a honeycomb epoxy glass fiber reinforced plastic antenna. The metallization process comprises a sequential technological process of antenna surface sealed modification treatment and antenna pre-treatment, oil-removing coarsening and modified sealed material coarsening and antenna metallization, and chemical formation of a metal film, electroplating and thickening and three-proofing post-treatment of a metal film layer. After being metalized, the honeycomb interlayer structure epoxy glass fiber reinforced plastic antenna has a metal appearance; surface conduction, heat conduction, magnetism conduction, solvent etching resistance, good conduction resistance and various electrical performance indexes can meet antenna design requirements. Compared with a conventional glass fiber reinforced plastic non-metal material metallization process, the antenna sealed modification treatment is simple in technological process and does not need special technological equipment including plasmas or laser induction and the like; the metallization process has high practicability and reliability and is convenient for use properties of promoting production and machining.

Description

technical field [0001] The invention relates to an epoxy fiberglass antenna, in particular to a metallization process for an epoxy fiberglass antenna with a honeycomb sandwich structure. Background technique [0002] Epoxy FRP is a composite material that has been developed rapidly for more than 50 years. It has superior performance and price ratio and is easy to be molded into complex product shapes. High environmental resistance, especially its high performance and low density make it have greater advantages than metal in many application fields. The honeycomb core material for the honeycomb epoxy fiberglass sandwich structure can be made of various materials, such as thermoplastic honeycomb, aluminum honeycomb, paper honeycomb, etc. [0003] An antenna is a metal device that radiates into space and receives electromagnetic waves from space in a radio transceiver system. However, the honeycomb sandwich structure epoxy glass fiber reinforced plastic material is a poor con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F17/00H01Q1/38C23C18/38C23C18/18C25D3/38C25D5/54C25D7/00
Inventor 夏奥利陆剑芳俞姚佳
Owner 36TH RES INST OF CETC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products