Wood softening liquid

A kind of softening liquid and wood technology, applied in wood treatment, impregnation of wood, wood impregnation, etc., can solve the problems of unable to meet the growing demand and low stability coefficient, and achieve the effect of high stability coefficient and crisp wood

Inactive Publication Date: 2014-05-07
常熟市鑫磊木业制造厂
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] After softening, traditional wood softeners have low stability coefficients and cannot meet the growing needs in daily wood processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A wood softening solution is characterized in that it consists of the following components:

[0022] 100 parts by mass of deionized water,

[0023] 2 mass parts sodium butyl ricinoleate sulfate,

[0024] 1 part by mass of hydroxypropyl methylcellulose,

[0025] 60 parts by mass of glycerol,

[0026] 18 parts by mass of boric acid,

[0027] 3 parts by mass of fatty alcohol polyoxyethylene ether,

[0028] 95 parts by mass of paraffin,

[0029] 1 part by mass of alcohol ether glycosides,

[0030] 4 parts by mass of sodium laureth sulfate,

[0031] 1 part by mass of alkylnaphthalene sulfonate,

[0032] 1 part by mass of polypropylene glycol,

[0033] 2 parts by mass of sodium lauramide ethyl sulfate.

Embodiment 2

[0035] A wood softening solution is characterized in that it consists of the following components:

[0036] 115 parts by mass of deionized water,

[0037] 3 parts by mass of sodium butyl ricinoleate,

[0038] 3 parts by mass of hydroxypropyl methylcellulose,

[0039] 70 parts by mass of glycerol,

[0040] 20 parts by mass of boric acid,

[0041] 4 parts by mass of fatty alcohol polyoxyethylene ether,

[0042] 100 parts by mass of paraffin,

[0043] 3 parts by mass of alcohol ether glycosides,

[0044] 5 parts by mass of sodium laureth sulfate,

[0045] 2 parts by mass of alkylnaphthalene sulfonate,

[0046] 2 parts by mass of polypropylene glycol,

[0047] 3 parts by mass of sodium lauroylaminoethyl sulfate.

Embodiment 3

[0049] A wood softening solution is characterized in that it consists of the following components:

[0050] 108 parts by mass of deionized water,

[0051] 2.3 parts by mass of sodium butyl ricinoleate,

[0052] 1.3 parts by mass of hydroxypropyl methylcellulose,

[0053] 65 parts by mass of glycerol,

[0054] 19 parts by mass of boric acid,

[0055] 3.4 parts by mass of fatty alcohol polyoxyethylene ether,

[0056] 98 parts by mass of paraffin,

[0057] 1.3 parts by mass of alcohol ether glycosides,

[0058] 4.5 parts by mass of sodium laureth sulfate,

[0059] 1.2 parts by mass of alkylnaphthalene sulfonate,

[0060] 1.2 parts by mass of polypropylene glycol,

[0061] 2.3 parts by mass of sodium lauramide ethyl sulfate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood softening liquid. The wood softening liquid is characterized by comprising the following components in parts by weight: 100-115 parts of deionized water, 2-3 parts of ricinoleic acid butyl ester sodium sulfate, 1-3 parts of hydroxypropyl methyl cellulose, 60-70 parts of glycerol, 18-20 parts of boric acid, 3-4 parts of fatty alcohol-polyoxyethylene ether, 95-100 parts of paraffin, 1-3 parts of alcohol ether glucoside, 4-5 parts of sodium laureth sulfate, 1-2 parts of alkyl naphthalene sulfonate, 1-2 parts of polypropylene glycol and 2-3 parts of sodium lauroyl aminoethyl. The wood softening liquid provided by the invention is high in stability coefficient and enables wood to be fragile easily.

Description

technical field [0001] The present invention relates to wood softening liquid. Background technique [0002] After softening, traditional wood softeners have low stability coefficients and cannot meet the increasing demands in daily wood processing. Contents of the invention [0003] The object of the present invention is to provide a kind of wood softening liquid, which has a high stability coefficient and is easy to make wood crisp. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of wood softening liquid, which is characterized in that it consists of the following components: [0005] 100-115 parts by mass of deionized water, [0006] 2-3 parts by mass of sodium butyl ricinoleate, [0007] 1-3 parts by mass of hydroxypropyl methylcellulose, [0008] 60-70 parts by mass of glycerol, [0009] 18-20 parts by mass of boric acid, [0010] 3-4 mass parts fatty alcohol polyoxyethylene ether, [0011] 95-1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/52B27K5/06
Inventor 黄建荣
Owner 常熟市鑫磊木业制造厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com