Alloy steel used for high-temperature electric resistance furnace
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high temperature resistance furnace and alloy steel technology, applied in the field of alloy steel, can solve the problem of high temperature resistance furnace, achieve high corrosion fatigue resistance, good high temperature oxidation resistance and oxidation resistance medium corrosion, reduce thermal conductivity and electrical conductivity rate and the effect of overheating sensitivity
Active Publication Date: 2014-06-18
扬州市金阳光铸造有限公司
View PDF6 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to provide an alloy steel for high temperature resistance furnace to solve the high temperature of high temperature resistance furnace, requiring alloy steel to have good heat resistance and wear resistance, heat strength performance and corrosionfatigue resistance, so as to ensure that the alloy steel can be used for a long time Problems with normal use
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] This embodiment provides an alloy steel for high-temperature resistance furnace, including components and the weight percentage of each component are as follows, C: 0.68%, Mn: 5.6%, Si: 0.65%, P: ≤0.03%, S : ≤0.025%, N: ≤0.12%, Cr: 13.1%, Ni: 1.4%, V: 0.30%, Mo: 0.9%, W: 2.5%, and the balance is Fe.
Embodiment 2
[0018] This embodiment provides an alloy steel for high-temperature resistance furnace, including components and the weight percentage of each component are as follows, C: 0.25%, Mn: 2.4%, Si: 0.40%, P: ≤0.03%, S : ≤0.025%, N: ≤0.12%, Cr: 12.3%, Ni: 2.7%, V: 0.25%, Mo: 1.2%, W: 3.2%, and the balance is Fe.
Embodiment 3
[0020] This embodiment provides an alloy steel for high-temperature resistance furnace, including components and the weight percentage of each component are as follows, C: 0.40%, Mn: 3.8%, Si: 0.51%, P: ≤0.03%, S : ≤0.025%, N: ≤0.12%, Cr: 12.3%, Ni: 2.6%, V: 0.26%, Mo: 1.0%, W: 2.7%, and the balance is Fe.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides an alloy steel used for high-temperature electric resistance furnace. The alloy steel is composed of the following components in percentage by weight: 0.25 to 0.68% of C, 2.4 to 5.6% of Mn, 0.40 to 0.65% of Si, not more than 0.03% of P, not more than 0.025% of S, not more than 0.12% of N, 12.3 to 13.1% of Cr, 1.4 to 2.7% of Ni, 0.25 to 0.30% of V, 0.9 to 1.2% of Mo, 2.5 to 3.2% of W, and the balance being Fe. The alloy steel used for high-temperature electric resistance furnace has a good high-temperature antioxidant performance and oxidant resistant performance, excellent wear resistant property, heat resistance, and antioxidant property, and a high corrosion fatigue resistant performance. Moreover the thermal conductivity, conductivity, and overheating sensitivity of the alloy steel are all reduced.
Description
technical field [0001] The invention relates to an alloy steel, in particular to an alloy steel used in a high-temperature resistance furnace. Background technique [0002] For alloy steel such as steel plate and section steel used in high temperature resistance furnace, due to the high temperature of high temperature resistance furnace, the alloy steel is required to have good heat resistance, wear resistance, heat strength and corrosionfatigue resistance, so as to ensure that the alloy steel can be used normally for a long time , At the same time, the overall performance of the alloy steel affects the safety of the production and use process of the high temperature resistance furnace. Therefore, the above problems should be considered and solved in the design and production process of the alloy steel used in the high temperature resistance furnace. Contents of the invention [0003] The purpose of the present invention is to provide an alloy steel for high temper...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.