Stone needle ceramic tile and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of ceramic tiles and meteorites, applied in the field of building ceramic materials, can solve the problems of no health care function, achieve low water absorption, improve the living environment, and regulate metabolism
Active Publication Date: 2014-07-30
安徽省亚欧陶瓷有限责任公司
View PDF3 Cites 12 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the rapid development of the real estate industry, the production and consumption of ceramic tiles have been greatly developed. However, the ceramic tiles currently on the market are only used for decoration and have no health care function. Health care tiles in places, used to improve people's physical fitness and purify the environment, will have huge social and economic benefits
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0016] A Bianstone ceramic brick made from the following raw materials (kg): silicon micropowder 40, obsidian 30, sillimanite 25, sea sand 20, burnt gemstone 22, magnesite 18, bamboo charcoal powder 8, meteorite powder 12. Magnetic powder 8, modified clay 28, red mud 6, phosphate slag 4, volcanic ash 8;
[0017] The preparation method of described modified clay is as follows: a, take attapulgite, diatomaceous earth, bentonite by mass ratio 6:4:2, mix uniformly, add appropriate amount of water to make the clay slurry that concentration is 38%, then Use sulfuric acid solution with a concentration of 22% to adjust the pH of the slurry to 4, heat in a water bath to 90°C, stir for 3 hours, filter, wash with distilled water until neutral, dry, calcinate at 465°C for 3 hours, pulverize, and pass through a 250-mesh sieve; b. The weight ratio is 1:2.5. Take the above-mentioned treated clay and mix it with a concentration of 2mol / L titanium tetrachloride aqueous solution, and th...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
flexural strength
aaaaa
aaaaa
water absorption
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a stone needle ceramic tile and a preparation method thereof. The stone needle ceramic tile is prepared from the following raw materials in parts by weight: 35-45 parts of a silica micropowder, 25-35 parts of obsidian, 20-30 parts of sillimanite, 15-25 parts of sea sand, 18-26 parts of flint clay, 12-24 parts of magnesia, 6-14 parts of a bamboo charcoal powder, 10-15 parts of a stone needle powder, 5-10 parts of a magnetic powder, 22-34 parts of modified clay, 4-8 parts of red mud, 3-6 parts of phosphorus ore slag, and 5-10 parts of volcano ash. The stone needle powder, the bamboo charcoal powder and the magnetic powder are added into the ceramic tile, so that the ceramic tile has higher health care value, can produce far infrared rays, ultrasonic pulses, magnetic fields and negative ions, not only can promote blood micro-circulation, regulates metabolism, improves human body immunity, also can adsorb and decompose various free harmful substances, kills bacteria, purifies air, and improves a living environment; and the prepared ceramic tile has the characteristics of high strength, low water absorption rate, good abrasion resistance, good weather resistance and the like, and is durable in use.
Description
technical field [0001] The invention relates to a meteorite ceramic brick and a preparation method thereof, belonging to the field of building ceramic materials. Background technique [0002] Ceramic bricks are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, powder making, molding, sintering and other processes. They are widely used in decoration and protection of walls of buildings and structures. face and ground. With the rapid development of the real estate industry, the production and consumption of ceramic tiles have been greatly developed. However, the ceramic tiles on the market are only used for decoration and have no health care function. The health care tiles in the place are used to improve people's physical fitness and purify the environment, and will have huge social and economic benefits. Contents of the invention [0003] The object of the present invention is to ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.