Vinylidene chloride floor coating

A technology of floor coating and perchloroethylene, applied in the direction of coating, etc., can solve the problems of non-wear resistance, easy to be corroded by acid and alkali, poor water resistance and cold resistance, etc., and achieve the effect of good wear resistance.

Active Publication Date: 2014-09-10
苏州靖羽新材料有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above technical problems, this application provides a perchlorethylene floor coating, which solves the technical problems of the existing perchlorethylene floor coatings such as poor water resistance and cold resistance, easy to be corroded by acid and alkali, and not wear-resistant.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of perchlorethylene ground coating, its raw material proportioning by weight is as follows: 100 parts of perchlorethylene resin; 5 parts of melamine; 30 parts of dibutyl phthalate; 1 part of formaldehyde; 25 parts of barium ricinoleate; 20 parts of alcohol; 40 parts of deionized water; 35 parts of xylene; 10 parts of pigment; 5 parts of titanium dioxide; 20 parts of antimony oxide; 15 parts of methanol; 10 parts of plasticizer; 25 parts of bentonite; 20 parts of talc; 15 servings.

[0016] After dissolving styrene in deionized water, add iron oxide red, barium ricinoleate, and ball mill for 30 minutes with a ball mill, then add antimony oxide, perchlorethylene resin, melamine, dibutyl phthalate, formaldehyde and butanol, and ball mill for 30 minutes , adding xylene and the remaining raw materials, after ball milling for 1h, filter the finished product with gauze.

[0017] The product has good wear resistance, 0.005g / cm2 for 1000 times of reciprocating testing ma...

Embodiment 2

[0019] A kind of perchlorethylene ground paint, its raw material proportioning by weight is as follows: 100 parts of perchlorethylene resin; 10 parts of melamine; 40 parts of dibutyl phthalate; 10 parts of formaldehyde; 35 parts of barium ricinoleate; 30 parts of alcohol; 60 parts of deionized water; 45 parts of xylene; 20 parts of pigment; 15 parts of titanium dioxide; 40 parts of antimony oxide; 25 parts of methanol; 30 parts of plasticizer; 45 parts of bentonite; 30 parts of talc; styrene 35 servings.

[0020] After dissolving styrene in deionized water, add iron oxide red, barium ricinoleate, and ball mill for 30 minutes with a ball mill, then add antimony oxide, perchlorethylene resin, melamine, dibutyl phthalate, formaldehyde and butanol, and ball mill for 30 minutes , adding xylene and the remaining raw materials, after ball milling for 1h, filter the finished product with gauze.

[0021] The product has good wear resistance, 0.003g / cm2 for 1000 times of reciprocating ...

Embodiment 3

[0023] A kind of perchlorethylene ground coating, its raw material proportioning by weight is as follows: 100 parts of perchlorethylene resin; 8 parts of melamine; 35 parts of dibutyl phthalate; 5 parts of formaldehyde; 30 parts of barium ricinoleate; 25 parts of alcohol; 50 parts of deionized water; 40 parts of xylene; 15 parts of pigment; 10 parts of titanium dioxide; 30 parts of antimony oxide; 20 parts of methanol; 20 parts of plasticizer; 35 parts of bentonite; 25 parts of talc; styrene 25 servings.

[0024] After dissolving styrene in deionized water, add iron oxide red, barium ricinoleate, ball mill for 30 minutes with a ball mill, add antimony oxide, perchlorethylene resin, melamine, dibutyl phthalate, formaldehyde and butanol, and ball mill for 30 minutes , adding xylene and the remaining raw materials, and after ball milling for 1h, filter the finished product with gauze.

[0025] The product has good wear resistance, 0.001g / cm2 for 1000 times of reciprocating testi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vinylidene chloride floor coating comprising the following raw materials in parts by weight: 100 parts of vinylidene chloride resin, 5-10 parts of melamine, 30-40 parts of dibutyl phthalate, 1-10 parts of formaldehyde, 25-35 parts of barium ricinoleate, 20-30 parts of butanol, 40-60 parts of deionized water, 35-45 parts of dimethylbenzene, 10-20 parts of pigment, 5-15 parts of titanium dioxide, 20-40 parts of antimony oxide, 15-25 parts of methanol, 10-30 parts of plasticizer, 25-45 parts of bentonite, 20-30 parts of talcum powder and 15-35 parts of styrene. The vinylidene chloride floor coating is good in wear resistance (up to 0.001-0.005g / cm<2> after being tested 1000 times by using a reciprocating tribometer), free of abnormalities after being soaked into 20-DEG C water for 10-20 days and capable of resisting to the temperature of 10 DEG C below zero for 10 hours without embrittling and cracking; in addition, a film has no abnormalities after being soaked into alkaline water for 5-7 days, so that the vinylidene chloride floor coating can be widely produced and used for continuously replacing existing material.

Description

technical field [0001] The application belongs to the field of coatings, in particular to a perchlorethylene floor coating. Background technique [0002] Paint, traditionally called paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, oil, or emulsion, with or without adding pigments, fillers, adding Corresponding additives, viscous liquid prepared with organic solvent or barium ricinoleate. Perchlorethylene organic compound, also known as perchlorethylene, is a compound formed by replacing all hydrogen atoms in ethylene with chlorine. Insoluble in water, miscible in most organic solvents such as ethanol and ether. It is mainly used as a solvent, such as dry cleaning solvent in dry cleaning, etc. Paint is a material that can be well bonded to the base material and form a complete and tough protective film on the surface of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D7/12
Inventor 钱玉珠
Owner 苏州靖羽新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com