Ni/nif2 reference electrode for molten salt of fluoride and manufacturing method thereof

A reference electrode, fluoride technology, applied in the direction of material electrochemical variables, etc., can solve the problems of poor stability of the reference electrode, long ion conduction time, and expensive production, and achieve good reproducibility and stability. , long service life, simple processing effect

Active Publication Date: 2016-05-11
SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by this invention is to overcome the Ni / NiF that is used in the high temperature fluoride molten salt in the prior art 2 The reference electrode has the defects of poor stability, short service life, complex structure and expensive production, and long ion conduction time. It provides a kind of electrode with good stability, long service life, short ion conduction time and simple structure. Ni / NiF in High Temperature Fluoride Molten Salt System 2 Reference electrode and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ni/nif2 reference electrode for molten salt of fluoride and manufacturing method thereof
  • Ni/nif2 reference electrode for molten salt of fluoride and manufacturing method thereof
  • Ni/nif2 reference electrode for molten salt of fluoride and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Such as Figure 1 ~ Figure 3 As shown, the present embodiment provides a kind of Ni / NiF for high temperature fluoride molten salt system 2 The reference electrode comprises a nickel wire electrode 1, an insulating sleeve 2 and a sealing plug 3; the nickel wire electrode is fixedly connected to the sealing plug, and the insulating sleeve 2 is equipped with a reference salt 6 for the sealing plug. To seal the insulating sleeve, the bottom end of the nickel wire electrode is immersed in the reference salt in the insulating sleeve; the outer wall of the insulating sleeve is provided with an arc groove 4, and the bottom of the arc groove is provided with a Through hole 5; through hole 5 is used as a salt bridge, so that the reference salt in the insulating casing and the high-temperature fluoride molten salt outside the insulating casing realize ion conduction; the surface roughness of the arc-shaped groove is 4 μm, The curvature radius R of the arc-shaped groove is 10mm; t...

Embodiment 2

[0051] In this example Ni / NiF 2 The Ni / NiF of embodiment 1 on the reference electrode structure 2 The reference electrode is similar, the difference lies in the parameters of each component.

[0052] A kind of mixed reference salt composed of FLINAK molten salt and nickel fluoride, nickel wire, zirconia doped boron nitride composite material as basic raw materials to prepare Ni / NiF 2 The method of reference electrode, comprises the following steps:

[0053] (1) Accurately weigh 10 grams of lithium fluoride, sodium fluoride, potassium fluoride, and nickel fluoride with a molar ratio of 37.2:9.2:33.6:20, put the above four fluorides into an agate mortar and grind them Mix well, put into graphite crucible, heat up from room temperature to 350°C at 5°C / min, dry under reduced pressure at 350°C for 10 hours, cool naturally, then grind into powder in agate mortar and put into reagent bottle spare;

[0054] (2) Take 7cm of nickel wire (99.98% purity) with a diameter of 1mm, heat i...

Embodiment 3

[0060] In this example Ni / NiF 2 The Ni / NiF of embodiment 1 on the reference electrode structure 2 The reference electrode is similar, the difference lies in the parameters of each component.

[0061] A kind of mixed reference salt composed of FLINAK molten salt and nickel fluoride, nickel wire, zirconia doped boron nitride composite material as basic raw materials to prepare Ni / NiF 2 The method of reference electrode, comprises the following steps:

[0062] (1) Accurately weigh 10 grams of lithium fluoride, sodium fluoride, potassium fluoride, and nickel fluoride with a molar ratio of 44.175:10.925:39.9:5, put the above four fluorides into an agate mortar and grind them Mix well, put into graphite crucible, heat up from room temperature to 350°C at 5°C / min, dry under reduced pressure at 350°C for 10 hours, cool naturally, then grind into powder in agate mortar and put into reagent bottle spare;

[0063] (2) Take 7cm of nickel wire (99.98% purity) with a diameter of 1mm, he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a Ni / NiF2 reference electrode used for molten fluoride, and a making method thereof. The Ni / NiF2 reference electrode comprises a nickel wire electrode, an insulation sleeve and a sealing plug used for sealing the insulation sleeve; the bottom of the insulation sleeve is provided with a reference salt; the nickel wire electrode is fixed to the sealing plug, and one end of the nickel wire electrode traverses through the sealing plug, extends into the insulation sleeve and is immersed in the reference salt; the outer sidewall of the insulation sleeve is provided with an arc-shaped groove, and the bottom of the arc-shaped groove is provided with a through hole; the surface roughness Ra of the arc-shaped groove is less than 12.5[mu]m, and the radius of curvature of the arc-shaped groove is not less than 2mm; and the diameter of the through hole is 0.05-0.3mm, and the depth of the through hole is 0.3-2.0mm. The Ni / NiF2 reference electrode has the advantages of short ion conduction time, and good reappearance and stability of the electrode potential.

Description

technical field [0001] The invention relates to a kind of Ni / NiF used in high temperature fluoride molten salt system 2 Reference electrode and its manufacturing method. Background technique [0002] Electrochemical research in high-temperature molten salt system is of great significance in both basic research and industrial production, and the reference electrode plays a vital role in the accurate measurement of electrochemical parameters. In the electrochemical research and production of fluoride molten salt system, a bottleneck problem is how to prepare a reference electrode with stable performance, good reproducibility and long service life. The commonly used reference electrode in fluoride molten salt is Ni / NiF with hot-pressed boron nitride as the sleeve. 2 Reference electrode, Ni / NiF with lanthanum fluoride single crystal as diaphragm material 2 Reference electrode, or insert Pt, W and other inert metals directly into the molten salt as a quasi-reference electrode....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/30
Inventor 郑海洋蒋锋黄卫田丽芳佘长锋龙德武李晴暖
Owner SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com