A method for curing self-lubricating spherical plain bearings using release shrink film

A joint bearing and shrink film technology, applied in sliding contact bearings, etc., can solve problems such as unsatisfactory coupling accuracy of the outer ring spherical surface, damage to the health of operators, and low service life of bearings, and achieve low cost, high production efficiency, and The effect of high tear strength

Active Publication Date: 2016-09-07
FUJIAN LONGXI BEARING (GROUP) CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Problems in this method: 1. The release agent coated on the outer spherical surface of the inner ring is attached to the outer spherical surface of the inner ring by soaking in a liquid release agent, but it cannot ensure that a protective film with uniform thickness is formed on the spherical surface, resulting in coating The layer is uneven, and when it is in contact with the sticky fabric pad, it will be partially unable to be released from the mold when it is cured, resulting in curing failure; 2. In order to prevent the above-mentioned local non-release situation, it needs to be soaked multiple times, generally more than three times , the processing efficiency is low; 3. Even if the method of multiple soaking is adopted, spherical friction will occur during the assembly process of putting the inner ring into the outer ring, and part of the release agent coating layer on the outer spherical surface of the inner ring will still be scratched Wipe off, resulting in poor demoulding effect or even curing failure; 4. The release agent is expensive, and it is a volatile chemical, which pollutes the environment and is harmful to the health of operators; 5. The existing processing methods cannot To obtain the required radial clearance after the bearing is cured, it is necessary to replace the inner ring with a smaller outer ball diameter, which is inefficient, and because the outer spherical surface tolerance of the inner ring for curing and the newly replaced inner ring is not the same may be exactly the same, so it will cause the final spherical coupling accuracy of the inner and outer rings to be unsatisfactory, which will eventually lead to a low service life of the bearing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0038] Choose a self-lubricating joint bearing with an inner diameter of 100 mm, an outer diameter of 150 mm, an inner ring width of 70 mm, an outer ring width of 55 mm, and an inner ring outer ball diameter of 130 mm. The radial clearance range of the bearing is 0.04 ~ 0.12 mm.

[0039] According to the radial clearance range of the bearing is 0.04 ~ 0.12 mm and the median value is 0.08 mm, a multi-layer co-extruded polyolefin heat shrinkable film with a thickness of 0.04 mm can be selected, which is the median value of the radial clearance range of the bearing 0.08 mm Half of the selection; made into a cylinder with a diameter of 135 mm, the diameter of the cylinder is selected according to the diameter of the inner ring and outer ball of 130 mm and increased by 5 mm.

[0040] Put the cylindrical release shrink film on the outer spherical surface of the inner ring, and the center line of the cylindrical release shrink film coincides with the center line of the inner ring;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for solidifying a self-lubricating joint bearing by using a release shrink film, which comprises: making the release shrink film into a cylindrical shape; placing the cylindrical release shrink film on the outer spherical surface of the inner ring; The inner ring of the release shrink film is baked in an oven so that the release shrink film shrinks and sticks tightly to the outer spherical surface of the inner ring; paste the PTFE fabric gasket to the inner spherical surface of the outer ring, and then put the inner ring into the In the outer ring; cure the inner ring and the outer ring with the liner together; rotate the cured self-lubricating joint bearing inner ring around the radial direction of the outer ring by 60°~90°, remove the release shrink film, Make the self-lubricating joint bearing form the required uniform radial clearance value. It has the following advantages: the release shrink film can effectively protect the outer spherical surface of the inner ring from bonding with the PTFE fabric liner during the curing process; the release shrink film has good toughness and will not It is scratched and damaged, and it is guaranteed to be completely released from the mold.

Description

technical field [0001] The invention relates to a method for solidifying a self-lubricating joint bearing by using a release shrink film. Background technique [0002] In the existing self-lubricating joint bearings, the front and back sides of the PTFE fabric liner are coated with adhesive. The release agent is coated on the outer spherical surface of the inner ring. In addition, self-lubricating spherical plain bearings usually require a certain radial clearance, but the radial clearance between the inner and outer rings after the existing processing method is cured is basically zero, so it is necessary to remove the cured inner ring from Take out the outer ring, and then replace the inner ring with a smaller outer ball diameter according to the design radial clearance requirements of the bearing. The difference in diameter of the inner ball is the radial clearance value of the bearing. [0003] Problems in this method: 1. The release agent coated on the outer spherical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16C23/02
Inventor 陈志雄王炳维颜杨丰陈朱池
Owner FUJIAN LONGXI BEARING (GROUP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products