Anticorrosive material

A technology of anti-corrosion materials and raw materials, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of large environmental pollution, poor substrate adhesion, low curing content, etc., and achieve the effect of good surface toughness, high curing content and strong adhesion

Inactive Publication Date: 2014-11-26
QINGDAO UWELL INFORMATION TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main problems of existing anti-corrosion materials are: poor adhesion to the substrate, low curing content, and large environmental pollution, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Example 1, an anticorrosive material, made of the following parts by weight of raw materials: 70 parts of polymer resin; 3 parts of additives; 10 parts of mixed solvents; 3 parts of pigments; 15 parts of fillers; hexamethylphosphoric triamide 3 parts; 45 parts of hollow glass beads; 15 parts of curing agent.

Embodiment 2

[0008] Example 2, an anticorrosive material, made of the following parts by weight: 60 parts of polymer resin; 3 parts of additives; 15 parts of mixed solvents; 1 part of pigments; 15 parts of fillers; hexamethylphosphoric triamide 3 parts; 45 parts of hollow glass beads; 15 parts of curing agent.

Embodiment 3

[0009] Example 3, an anticorrosive material, made of the following parts by weight of raw materials: 65 parts of polymer resin; 2 parts of additives; 20 parts of mixed solvents; 3 parts of pigments; 25 parts of fillers; hexamethylphosphoric triamide 5 parts; 25 parts of hollow glass beads; 20 parts of curing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anticorrosive material which is prepared from the following raw materials in parts by weight: 60-70 parts of high polymer resin, 2-3 parts of an assistant, 10-20 parts of mixed solvents, 1-3 parts of pigment, 15-25 parts of filler, 3-5parts of hexamethylphosphoramide, 25-45 parts of hollow glass bead and 15-20 parts of a curing agent. The anticorrosive material has the advantages of good leveling property, no pinhole, good surface tenacity, strong adhesive force, high curing component, good environmental friendliness and the like.

Description

Technical field [0001] The invention relates to the field of anti-corrosion materials, in particular to an anti-corrosion material. Background technique [0002] With the rapid development of China’s economic construction, construction, transportation, petrochemicals, energy, machinery and other fields have achieved rapid growth. With the rapid economic development, environmental pollution has become more and more serious. Corrosion is getting more and more serious. According to incomplete statistics, the annual direct economic loss caused by corrosion accounts for about 1%-4% of the total national economic output; therefore, it provides a broad development space for anti-corrosion materials. At present, the existing anti-corrosion materials mainly have problems: poor adhesion to the substrate, low curing content, and large environmental pollution. Summary of the invention [0003] In view of the shortcomings of the prior art, the technical problem to be solved by the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/08C09D7/12
Inventor 张涛
Owner QINGDAO UWELL INFORMATION TECH