Sealant for photovoltaic module and preparation method of sealant

A photovoltaic module and sealant technology, applied in the sealant field, can solve the problems of metal corrosion and imperfect sealing performance, and achieve the effects of good weather resistance, high ultraviolet resistance performance and simple production method

Active Publication Date: 2014-12-03
特瓦特能源科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, ordinary one-component silicone solar photovoltaic sealant is used in the market; the main disadvantage of this glue is that it takes about 24 hours to cure, the sealing performance is not perfect, and it has a certain corrosion effect on metals.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The sealant for photovoltaic modules is characterized in that it is made of the following raw materials in parts by weight: E-51 epoxy resin: 100 parts, 201 polysulfide rubber: 15-25 parts, m-phenylenediamine: 10-15 parts, dibutyl phthalate: 10-20 parts, diethylenetriamine: 1-3 parts, talcum powder: 30-50 parts, maleic anhydride: 10-15 parts, 651 low molecular weight Polyamide: 15-20 parts, stannous octoate: 4-6 parts, propylene oxide phenyl ether or resorcinol diglycidyl ether or ethylene glycol diglycidyl ether: 20-30 parts.

Embodiment 2

[0019] The sealant for photovoltaic modules is characterized in that it is made of the following raw materials in parts by weight: E-51 epoxy resin: 100 parts, 201 polysulfide rubber: 20 parts, m-phenylenediamine: 13 parts , Dibutyl phthalate: 15 parts, Diethylene triamine: 2 parts, Talc powder: 40 parts, Maleic anhydride: 13 parts, 651 low molecular weight polyamide: 18 parts, Stannous octoate: 5 parts , Propylene oxide phenyl ether or resorcinol diglycidyl ether or ethylene glycol diglycidyl ether: 25 parts.

Embodiment 3

[0021] The sealant for photovoltaic modules is characterized in that it is made of the following raw materials in parts by weight: E-51 epoxy resin: 100 parts, 201 polysulfide rubber: 15 parts, m-phenylenediamine: 10 parts , Dibutyl phthalate: 10 parts, Diethylene triamine: 1 part, Talc powder: 30 parts, Maleic anhydride: 10 parts, 651 low molecular weight polyamide: 15 parts, Stannous octoate: 4 parts , Propylene oxide phenyl ether or resorcinol diglycidyl ether or ethylene glycol diglycidyl ether: 20 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of sealants and relates to a sealant for a photovoltaic module. The sealant is characterized by comprising the following raw materials in parts by weight: 100 parts of E-51 epoxy resin, 15-25 parts of 201 polysulfide rubber, 10-15 parts of m-phenylenediamine, 10-20 parts of dibutyl phthalate, 1-3 parts of diethylenetriamine, 30-50 parts of talc power, 10-15 parts of maleic anhydride, 15-20 parts of 651 low-molecular-weight polyamide, 4-6 parts of stannous octoate and 20-30 parts of epoxypropane phenyl ether or diglycidyl resorcinol ether or ethylene glycol diglycidyl ether. The invention also discloses a preparation method of the sealant. The sealant disclosed by the invention has the beneficial effects of convenience in operation, short curing time, good adhesion, low water vapor and gas permeability, good sealing property / weather resistance and UV resistance and wide application temperature range and the long-term performance is maintained.

Description

Technical field [0001] The present invention belongs to the field of sealing gel technology, especially the sealing and preparation methods involved in photovoltaic components. This sealing glue is mainly used for sealing of solar cell components. Background technique [0002] With the continuous improvement of the conversion rate of green and environmentally friendly solar power, the market's demand for solar photovoltaic components is increasing, and the assembly set achievements between solar photovoltaic components are extremely important.Global can no longer be suitable for the assembly integration of solar photovoltaic components such as adhesion and aging resistance.The existing dual -group contraction sealing has a large defects in aging resistance, ultraviolet, adhesion and flame retardant performance. It is not suitable for the field of photovoltaic component sealing and areas with high bonding requirements. [0003] At present, the general single -component organic sil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09K3/10
Inventor 尹红
Owner 特瓦特能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap