Colored gloss coating for ceramic

A glossy coating and colored technology, applied in the direction of coating, etc., can solve the problems of low hardness, poor chemical resistance and water resistance

Inactive Publication Date: 2014-12-10
SUZHOU SHENGPULA NEW MATERIAL SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above technical problems, the present application provides a colored gloss coating for ceramics, which solves the technical problems of existing colored gloss coatings for ceramics such as low gloss, low hardness, poor chemical resistance and water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of colored luster coating for ceramics, its raw material ratio is as follows in parts by weight: 100 parts of butyl acrylate; 10 parts of polypropylene glycol; 35 parts of olive oil; 15 parts of 2,4-benzophenone diisocyanate; 80 parts of water ; 15 parts of hydroxyethyl acrylate; 5 parts of iron oxide red; 20 parts of N-vinylpyrrolidone; 5 parts of potassium soap; 40 parts of triisocyanate; 1 part of hexamethoxymethyl melamine; 1 part of benzoin ether; 3 parts of benzophenone; 5 parts of clay.

[0014] After the above raw materials are mixed uniformly in the reaction kettle, they are coated on ceramics and calcined at 300°C for 30 minutes.

[0015] The gloss of the product is 100%, the hardness is 5H; the surface dry time is 40s, and it is hard to dry for 30 minutes. After soaking in water for 30 days, there is no foaming or shedding phenomenon; after soaking in saturated calcium hydroxide for 10 days, there is no foaming or wrinkling; no discoloration after 100 ...

Embodiment 2

[0017] A kind of colored luster paint for ceramics, its raw material ratio is as follows in parts by weight: 100 parts of butyl acrylate; 30 parts of polypropylene glycol; 55 parts of olive oil; 25 parts of 2,4-benzophenone diisocyanate; 100 parts of water 35 parts of hydroxyethyl acrylate; 15 parts of medium chrome yellow; 40 parts of N-vinylpyrrolidone; 15 parts of potassium soap; 50 parts of triisocyanate; 5 parts of hexamethoxymethyl melamine; 10 parts of benzoin ether; 7 parts of benzophenone; 25 parts of clay.

[0018] After the above raw materials are mixed uniformly in the reaction kettle, they are coated on ceramics and calcined at 400°C for 40 minutes.

[0019] The gloss of the product is 110%, and the hardness is 6H; the surface drying time is 35s, and the hard drying time is 25 minutes. After soaking in water for 45 days, there is no foaming or shedding phenomenon; after soaking in saturated calcium hydroxide for 15 days, there is no foaming or wrinkling; no discol...

Embodiment 3

[0021] A kind of colored luster paint for ceramics, its raw material ratio is as follows in parts by weight: 100 parts of butyl acrylate; 20 parts of polypropylene glycol; 45 parts of olive oil; 20 parts of 2,4-benzophenone diisocyanate; 90 parts of water ; 25 parts of hydroxyethyl acrylate; 10 parts of iron oxide red; 30 parts of N-vinylpyrrolidone; 10 parts of potassium soap; 45 parts of triisocyanate; 3 parts of hexamethoxymethyl melamine; 5 parts of benzoin ether; 5 parts of benzophenone; 15 parts of clay.

[0022] After the above raw materials are mixed uniformly in the reaction kettle, they are coated on ceramics and calcined at 350°C for 35 minutes.

[0023] The gloss of the product is 120%, and the hardness is 7H; the surface drying time is 30s, and it is hard to dry for 20 minutes. After soaking in water for 60 days, there is no foaming and shedding phenomenon; after soaking in saturated calcium hydroxide for 20 days, there is no foaming and wrinkling; no discoloratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colored gloss coating for ceramic. The colored gloss coating comprises the following raw materials in parts by weight: 100 parts of butyl acrylate, 10-30 parts of polypropylene glycol, 35-55 parts of olive oil, 15-25 parts of 2,4-benzophenone diisocyanate, 80-100 parts of water, 15-35 parts of hydroxyethyl acrylate, 5-15 parts of coloring pigment, 20-40 parts of N-vinyl pyrrolidone, 5-15 parts of potash soap, 40-50 parts of triisocyanate, 1-5 parts of cross-linking agent, 1-10 parts of benzoin diethyl ether, 10-20 parts of urea, 3-7 parts of benzophenone and 5-25 parts of clay. The gloss of the colored gloss coating is 100-120%, the hardness of the colored gloss coating is 5-7H, the surface drying time of the colored gloss coating is 30-40 seconds, the hard drying time is 20-30 minutes, no foaming or dropping phenomenon is generated after the colored gloss coating is soaked in water for 30-60 days, no bubble or shrinkage is generate after the colored gloss coating is soaked in saturated calcium hydroxide for 10-20 days, no color change or powdering phenomenon after the colored gloss coating is radiated for 100 hours in ultraviolet light, and the colored gloss coating can be widely produced to replace conventional materials.

Description

technical field [0001] The application belongs to the field of coatings, in particular to a colored and glossy coating for ceramics. Background technique [0002] Ceramics is the general term for pottery and porcelain. Humans invented pottery as early as the Neolithic Age, about 8000 BC. Ceramic materials are mostly oxides, nitrides, borides and carbides. Common ceramic materials are clay, alumina, kaolin and so on. Ceramic materials generally have higher hardness, but poor plasticity. In addition to the use of tableware and decoration, it also plays an important role in the development of science and technology. The raw material of ceramics is obtained by quenching the earth's original large resource clay. The nature of clay is tough, it can be molded when it meets water at room temperature, it can be carved when it is slightly dry, and it can be ground when it is completely dry; it can be made into pottery when it is fired to 700 degrees, and it can be filled with wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D7/12C09D1/00
Inventor 费金华
Owner SUZHOU SHENGPULA NEW MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com