Manufacture method of special-shaped composite material rib

The technology of a composite material and a manufacturing method is applied in the manufacturing field of rib parts, which can solve the problems of uneven web surface of rib parts, and achieve the effects of smooth web surface, easy use and low cost.

Inactive Publication Date: 2015-03-25
CHENGDU AIRCRAFT INDUSTRY GROUP
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the problem that the web surface of the rib part is uneven due to the restriction of fiber slippage during the curing process of the rib part when the vacuum bag-autoclave method is currently used to manu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture method of special-shaped composite material rib
  • Manufacture method of special-shaped composite material rib
  • Manufacture method of special-shaped composite material rib

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Example

[0043] Such as Figure 2~6 As shown, the manufacturing method of the present invention needs to use two sets of tooling molds, one is a soft mold forming mold to prepare the soft mold 12, and the other is a part forming mold to prepare the rib part of the present invention. The rib part includes a web 1 and a flange 2, such as figure 2 As shown, the web 1 and the flange 2 are an integral structure, and the rib part is an axisymmetric structure.

[0044] The soft mold forming mold includes a support seat 4, and a soft mold forming male mold 3 for forming a soft mold 12 is also provided on the support seat 4, such as image 3 Shown. When a soft mold forming mold is used to prepare the soft mold 12, a rubber sheet is laid on the soft mold forming male mold 3, and the rubber sheet forms a rubber sheet layer. The rubber sheet layer in this embodiment is two layers. The rubber sheet is used to form a soft mold 12 with the same structure as the rib part, and the soft mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacture method of a special-shaped composite material rib. The manufacture method comprises the following steps: (1) preparing a flexible mold molding mold and a part molding mold respectively; (2) preparing a flexible mold by utilizing the flexible mold molding mold; (3) assembling a rib part blank and the flexible mold to a part molding mold to prepare a rib part; and (4) demolding. The manufacture method not only is simple in step, but also is convenient to use, and also can guarantee the levelness of a web panel of the rib part, so that the manufacture method is suitable for popularization and use.

Description

Technical field [0001] The invention relates to a method for manufacturing rib parts, in particular to a method for manufacturing special-shaped composite material ribs. Background technique [0002] At present, the vacuum bag-autoclave method is the most commonly used method for manufacturing high-performance composite parts. figure 2 The rib-shaped parts shown are often laid on a male mold and then cured on the male mold. However, when manufacturing rib parts with a flange height exceeding 50mm, the web surface of the rib part is usually uneven due to the limitation of fiber slip during the curing process of the rib part, and the thickness of the web surface is uneven, resulting in uneven thickness ,Such as figure 1 Shown. Summary of the invention [0003] The purpose of the present invention is to overcome the current use of vacuum bag-autoclave method to manufacture rib parts with a flange height exceeding 50mm, usually due to the limitation of fiber slippage during the cur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/44B29C70/54B29C33/00
CPCB29C70/44B29C33/00B29C70/54
Inventor 程勇赵明马瑞
Owner CHENGDU AIRCRAFT INDUSTRY GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap