A welding process, door and window technology, applied in welding equipment, manufacturing tools, arc welding equipment, etc., can solve the problem of inability to guarantee the gap between the thickness of the aluminum corner code blanking and the cavity of the profile, and the inability to guarantee the strength, sealing and firmness of the corners In order to improve the service life and safety factor, the service life is long, and the heat cycle resistance is excellent.

Inactive Publication Date: 2015-04-01
QINGDAO DUANYI METAL
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The butt joints of the window corners made by the above two methods have the following disadvantages: 1. When the thickness of the profile cavity is too large or too small when the 45° aluminum corner code is assembled, it is impossible to ensure that the blanking thickness of the aluminum corner code is consistent with the profile cavity fit clearance
2. The firmness of the 90° self-tapping screw connection is not good, and the strength and sealing of the corner cannot be guaranteed
3. If the above two methods are improperly handled, there will be obvious butt wiring traces at the butt joints of the group corners, which not only affects the appearance, but also is easy to stick to dust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1, a door and window welding process, is characterized in that: comprising the following steps:

[0022] (1) Cold-press forming the metal plate in a metal door and window cold-pressing machine; the tail end of the metal door and window cold-pressing machine is provided with a roller mold with a thickness less than 2mm; align the two edge ends of a door and window profile, and Fine-tuning the seams;

[0023] (2) Grinding the surface of the doors and windows to be welded to remove the surface oxide film;

[0024] (3) Clean the parts to be welded with pickling passivation solution;

[0025] (4) Install the corner pads in the cavity of the door and window profiles and place the door and window profiles on the special clamping workbench, butt the corners, and position and press them with clamps;

[0026] (5) Argon arc welding treatment: Position the door and window profiles clamped on the workbench by spot welding; welding should start from the position of the e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a door window welding process which comprises the following steps: (1), performing cold-press moulding on a metal plate in a metal door window cold press, aligning the end parts of two edges of a door window section material, and performing fine adjustment on butt seams, wherein the tail end of the metal door window cold press is provided with a roller wheel mold with the thickness less than 2mm; (2) polishing the surface of a to-be-welded door window to remove a surface oxidation film; (3) cleaning a to-be-welded part with an acid-washing passivation solution. The invention provides the welding process of a door window which is excellent in heat-proof cycle performance, good in abrasion resistance and wearability performance, free from welded doorframe section material salient points and long in service life.

Description

technical field [0001] The invention relates to the technical field of door and window profiles, in particular to a door and window welding process. Background technique [0002] The currently known method of door frame profile welding is butt welding technology. Its operating principle is to first superimpose the two sides of the seam in the groove of the door frame, then use a butt welder to weld point by point along the gap at a certain interval. Seam to weld the seam well. Moreover, when this technology welds the groove junction of the door frame profile, many protruding and uneven solder spots will be produced. These raised solder spots will constantly rub against the glass installed in the groove when the glass door is opened and closed. And collisions, it is easy to crack the corners of the glass. In addition, the welding place of the door frame profile welded by this technology is not strong enough, easy to crack, and has a short service life. After the groove is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B23K9/16
CPCB23P15/00B23P2700/08
Inventor 吴胜杰
Owner QINGDAO DUANYI METAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap