Hot forging pressing process water meter copper shell and manufacturing method thereof

A manufacturing method and hot forging technology are applied in the hot forging process water meter copper shell and its manufacturing field, which can solve the problems of fracture, easy generation of small pores in the shell wall, insufficient shell strength, etc. Smooth appearance

Inactive Publication Date: 2015-04-08
宁波宁水仪表有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the above-mentioned technical problems, the object of the present invention is to provide a hot forging water meter copper shell and its manufacturing method, which solves the problem of small air holes in the shell wall and the hidden danger of fracture caused by insufficient shell strength in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot forging pressing process water meter copper shell and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The specific implementation manners of the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention.

[0029] The hot forging process water meter copper shell of the present invention comprises a hot forging process water meter copper shell and a manufacturing method thereof, comprising the following steps:

[0030] S1: Cutting copper rods with a diameter of φ60 to 75MM and a weight of 1600 to 1900 grams;

[0031] S2: Rapidly heat the copper rod that has passed through S1 to between 700 and 800 degrees through the heating furnace equipment;

[0032] S3: Put the copper bar material obtained in S2 into the stamping equipment and the special water meter copper shell mold for hot forging and stamping;

[0033] S4: trimming the copper shell blank that has passed through S3;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a hot forging pressing process water meter copper shell and a manufacturing method thereof. The manufacturing method comprises the following steps: S1, feeding a copper bar which has the diameter Pi of 60-75 MM, and weighs 1,600-1,900 g; S2, rapidly heating the copper bar obtained in the S1 through combustion heater equipment to be 700-800 DEG C; S3, putting the copper bar obtained in the S2 in stamping equipment to be subjected to hot forging stamping forming with a special water meter copper shell mold; S4, cutting edges of the copper shell blank obtained in the S3; S5, inspecting the edge-cut copper shell obtained in the S4 to obtain the needed hot forging pressing process water meter copper shell. The quantity of waste gas generated in the hot forging pressing process water meter copper shell blank forming process is smaller than that of waste gas generated in casting process, so that the environment protection is efficiently improved; the sealing performance of the shell wall in forging pressing of the hot forging pressing process water meter copper shell blank is improved, no small air holes are formed in the shell wall, a process of secondary infiltration for controlling the small air holes is eliminated, and the scrappage caused by the small air holes is reduced.

Description

technical field [0001] The invention relates to a water meter copper shell, in particular to a hot forging water meter copper shell and a manufacturing method thereof. Background technique [0002] At present, the water meter copper shells sold on the market are mainly cast water meter copper shells. The casting process water meter copper shell blanks generate a large amount of waste gas during casting, and the blank shell walls are prone to small pores during the casting process. Secondary impregnation after machining is required to control some of the small pores of the shell wall. The scrap amount of the blank due to small pores is less than 10%. The sealing of the shell wall of this blank and the mechanical strength of the entire shell are poor. There is a risk of fracture under high-strength collisions, and the inside and outside of the shell are not flat, and the surface is rough and does not meet the appearance requirements. After processing and forming, it will have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01F15/14
Inventor 伍杰辉
Owner 宁波宁水仪表有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap