High-plasticity cast aluminum alloy and pressure casting preparation method thereof

A casting aluminum alloy, high plasticity technology, applied in the field of casting aluminum alloy and its preparation, high plasticity casting aluminum alloy and its pressure casting preparation, can solve the problem of increasing alloy hot cracking and corrosion tendency, reducing casting performance, and limiting alloy application range and other issues, to achieve the effect of improving plasticity, high production efficiency, and fine grain size

Active Publication Date: 2015-04-29
SHANGHAI JIAO TONG UNIV
View PDF9 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the Cu element added to the Al-Si alloy will increase the hot cracking and corrosion tendency of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment relates to a high plasticity casting aluminum alloy and a preparation method thereof by pressure casting.

[0034] In the first aspect, this embodiment provides a high plasticity cast aluminum alloy, the composition (weight content) of the aluminum alloy is: 7.5% Si, 0.5% Mg, 0.2% Mn, 0.1% Ti, 0.05% Y, 0.6% Fe , 20ppm P, 100ppm Sr, other unavoidable impurities are less than 0.2%, and the rest is Al.

[0035]In the second aspect, this embodiment provides a method for preparing the high-plastic cast aluminum alloy by pressure casting, which includes the following steps:

[0036] The first step is to smelt the alloy to obtain an aluminum alloy melt; wherein, the specific steps of the process of smelting the alloy are: (1) Preheat the smelting raw material in an oven to 100° C. The bell jar and other surfaces are cleaned and derusted and coated with paint. The paint is made of 25% talcum powder and 5% water glass with an appropriate amount of water, and the...

Embodiment 2

[0040] This embodiment relates to a high plasticity casting aluminum alloy and a preparation method thereof by pressure casting.

[0041] In the first aspect, this embodiment provides a high-plasticity casting aluminum alloy, the composition (weight content) of the aluminum alloy is: 8.5% Si, 0.6% Mg, 0.3% Mn, 0.2% Ti, 1.5% Gd, 0.7% Fe , 40ppm P, 200ppm Sr, other unavoidable impurities are less than 0.2%, and the rest is Al.

[0042] In the second aspect, this embodiment provides a method for preparing the high-plastic cast aluminum alloy by pressure casting, which includes the following steps:

[0043] The first step is to smelt the alloy to obtain an aluminum alloy melt; wherein, the specific steps of the process of smelting the alloy are: (1) Preheat the smelting raw material in an oven to 200° C. The bell jar and other surfaces are cleaned and derusted and coated with paint. The paint is made of 25% talcum powder and 5% water glass with an appropriate amount of water, and...

Embodiment 3

[0047] This embodiment relates to a high plasticity casting aluminum alloy and a preparation method thereof by pressure casting.

[0048] In the first aspect, the present invention provides a high plasticity casting aluminum alloy, the composition (weight content) of the aluminum alloy is: 9.5% Si, 0.7% Mg, 0.4% Mn, 0.3% Ti, 0.1% Gd, 0.1% Y, 0.02% Nd, 0.8% Fe, 60ppm P, 300ppm Sr, other unavoidable impurities are less than 0.2%, and the rest is Al.

[0049] In the second aspect, this embodiment provides a method for preparing the high-plastic cast aluminum alloy by pressure casting, which includes the following steps:

[0050] The first step is to smelt the alloy to obtain an aluminum alloy melt; wherein, the specific steps of the process of smelting the alloy are: (1) Preheat the smelting raw material in an oven to 200° C. The bell jar and other surfaces are cleaned and derusted and coated with paint. The paint is made of 25% talcum powder and 5% water glass with an appropria...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-plasticity cast aluminum alloy and a pressure casting preparation method thereof, belonging to the technical fields of metal materials and metallurgy. The high-plasticity cast aluminum alloy comprises the following components in percentage by weight: 7.5-14.5% of Si, 0.5-0.8% of Mg, 0.2-0.5% of Mn, 0.1-0.4% of Ti, 0.01-1.5% of RE, 0.6-1.3% of Fe, at most 100 ppm of P, 100-600 ppm of Sr and the balance of Al. The RE is one or more of Gd, Y, Nd, Sm, Er, Yb and La. After the high-plasticity cast aluminum alloy is subjected to pressure casting, the elongation percentage delta of the alloy is greater than or equal to 20%. The alloy has the advantages of excellent casting performance and low cost. The method has the advantages of simple technique, high production efficiency and obvious progress, and widens the application range of the Al-Si cast aluminum alloy.

Description

technical field [0001] The invention relates to a casting aluminum alloy and a preparation method thereof, in particular to a high-plasticity casting aluminum alloy and a pressure casting preparation method thereof, belonging to the field of metal materials and metallurgy. Background technique [0002] As a traditional metal material, cast aluminum alloy is widely used in aviation, aerospace, automobile, machinery and other industries due to its low density and high specific strength. With the development of modern industry and new casting technologies, the demand for cast aluminum alloys, such as cast aluminum alloys with high strength, high plasticity, excellent wear resistance and corrosion resistance, is increasing. After decades of development, high-strength aluminum alloys have formed a complete series, with stable performance and increasingly perfect production methods, becoming an indispensable alloy system in the field of materials. However, the current high-streng...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/02C22C1/03C22C1/06B22D17/00
CPCB22D17/00C22C1/026C22C1/03C22C1/06C22C21/02
Inventor 王渠东隋育栋
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap