A high-strength coated Oxford cloth

A coating and high-strength technology, applied in the field of Oxford cloth, can solve problems such as uneconomical, expensive, and bulky, and achieve good practicability and the effect of inhibiting mold production

Active Publication Date: 2016-09-07
YANGZHOU JIYUAN TEXTILE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

3) PU glue is a good waterproof glue, which can reach about 800mm / square inch. It is generally used for outdoor tents, but the price is more expensive than acrylic glue
4) The waterproof effect of thick PU glue can reach about 1200mm / square inch, but because it is bulky and uneconomical, it is mostly used for raincoats, rain pants, etc.
5) Silver glue is made of silver dye and PU glue. Its skin is silver, smooth and finely woven with a little luster. It is mostly used for outer tents. It has a good waterproof effect and is beautiful, but the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength coated Oxford cloth
  • A high-strength coated Oxford cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below in conjunction with specific drawings.

[0021] Such as figure 1 and figure 2 As shown, the high-strength coated Oxford cloth includes base cloth 1, silica sol layer 2, acrylic resin coating 3, inorganic printing coating 4, polyurethane resin coating 5 and film layer 6; base cloth 1 is dipped in two In the silica sol layer 2, an acrylic resin coating 3, an inorganic printing coating 4, a polyurethane resin coating 5 and a film layer 6 are sequentially arranged outside the silica sol layer 2 from the inside to the outside; An acrylic resin coating 3 and a film layer 6 are sequentially provided from the inside to the outside. Base fabric 1, silica sol layer 2, acrylic resin coating 3, inorganic printing coating 4, polyurethane resin coating 5, and film layer 6 have a thickness ratio of 1:1-1.2:4-5:1-2 :1.5-2:0.1-0.5.

[0022] The base fabric 1 is an Oxford cloth woven with 500D polyester high-strength silk as raw ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-strength coating Oxford cloth. The high-strength coating Oxford cloth comprises base cloth, a silicon dioxide sol layer, an acrylic resin coating, an inorganic printing coating, a polyurethane resin coating and a film layer, wherein the base cloth is dipped into the silicon dioxide sol layer and the acrylic resin coating is arranged outside the silicon dioxide sol layer; the inorganic printing coating is arranged outside the acrylic resin coating; the polyurethane resin coating is arranged outside the inorganic printing coating; and the film layer is arranged outside the polyurethane resin coating. The gram weight of an Oxford cloth finished product is less than or equal to 300g / m<2>, the breaking strength in the warp direction is more than or equal to 2300N, the breaking strength in the weft direction is more than or equal to 2200N, the tearing strength in the warp direction is more than or equal to 300N, the tearing strength in the weft direction is more than or equal to 260N, the hydrostatic pressure flat part is more than or equal to 20kpa and the hydrostatic pressure fold part is more than or equal to 8kpa; the color fastness to light is more than or equal to 6-7 grades; and the high-strength coating Oxford cloth can resist sticking, has the advantages of resisting mold corrosion, inhibiting mold production, resisting salt mist corrosion and resisting natural ageing, so that the service life of a tent is more than 3 years.

Description

technical field [0001] The invention relates to the technical field of Oxford cloth, in particular to a high-strength coated Oxford cloth. Background technique [0002] Oxford cloth is a new type of fabric with various functions and a wide range of uses. The market mainly includes: nesting, full elastic, nylon, tigue and other varieties. As the performance of Oxford cloth becomes stronger and stronger, it has been widely used in tent cloth. The quality of the tent and the length of service life are closely related to the tent cloth. [0003] Conventional tent fabrics include nylon, TC cloth, silk silk, CORETEX, etc. in addition to canvas. Among them, canvas has strong water resistance, good heat insulation effect, and does not get hot when exposed to the sun, but it is hard and bulky, easy to absorb moisture, mold and fade easily, and its economic benefits are not as good as nylon. Nylon has strong tension, bright and smooth color, not easy to fade, soft texture, good stre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/40B32B27/30B32B33/00
CPCB32B27/06B32B33/00B32B2255/02B32B2255/20B32B2255/26B32B2255/28B32B2307/552B32B2307/5825B32B2307/7145
Inventor 薛齐全
Owner YANGZHOU JIYUAN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products