A kind of aluminum alloy structure material and preparation method thereof

A technology of structural materials and aluminum alloys, which is applied in the manufacture of ground vehicles and space vehicle structural products, low-density and high-strength aluminum alloy structural materials and their preparation fields, can solve the problems of inability to meet the design requirements for weight reduction, difficulty in the strength of structural materials, and Low strength and other problems, to achieve the effect of improving high-cost and complicated technical routes, scientific and reasonable formula design, and shortening the manufacturing process

Active Publication Date: 2017-09-26
NO 52 INST OF CHINA NORTH IND GRP CORP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to increase the strength, hot rolling + annealing treatment + large deformation cold hardening + stabilizing heat treatment process is adopted. As a result, the strength is further improved, but the plasticity of the material is often sacrificed, and the process is complicated and costly. It is only suitable for 2-3mm or less For other complex structural profiles, pipes, bars, forgings and large thickness plates and strips, it is difficult to process large deformation and cold work hardening, and it is difficult to improve the strength of structural materials, which greatly limits the application of high-strength aluminum alloy structural products. Development and Application
[0004] 7XXX series alloys such as 7A04, 7A09 and 7055 are high-strength alloys whose strength can reach 520-680MPa, but the density of such alloys is too large, about 2.78-2.86g / cm 3 , obviously not good for weight reduction design
Obviously, the density of the alloy is high, and the strength is as low as 379MPa, which cannot meet the design requirements for weight reduction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aluminum alloy structure material and preparation method thereof
  • A kind of aluminum alloy structure material and preparation method thereof
  • A kind of aluminum alloy structure material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] A method for preparing an aluminum alloy structural material, specifically:

[0060] 1. Alloy composition setting: (weight percentage):

[0061] AL-Mg-Si-Mn-Ti alloy:

[0062] Mg: 10.5% ~ 17.4%; and containing Be: 0.01% ~ 0.05%, based on magnesium charge;

[0063] Si: 1.0% to 5.0%;

[0064] Mn: 0.3% ~ 0.8%;

[0065] Ti: 0.15% to 0.25%;

[0066] Al: the balance of aluminum alloy and unavoidable impurities.

[0067] where the density estimate is calculated as:

[0068] The main contribution to the reduction of density ρ includes the combined effect of the contribution of the density value of each component element and the addition amount. Simplifies to:

[0069] ρ=G / Σ(W i / ρ i ) (1)

[0070] Where G is the total amount of the ingredient formula, which is calculated as 100% for the convenience of calculation;

[0071] W i Add weight percentage for each component in the ingredient formula;

[0072] ρ i is the density value of each component in the composition ...

Embodiment 1

[0118] The ingredient formulations of Example 1, Example 2 and Example 3 are shown in Table 1.

[0119] Table 1 each embodiment chemical composition (wt%)

[0120]

[0121] The mechanical performance characteristics of each embodiment are shown in Table 2.

[0122] The characteristics of mechanical properties of each embodiment of table 2

[0123] Example

R m / N / mm 2

R p-1 / N / mm 2

A / %

ρ / g / cm 3

Example 1

555

485

32

2.53

Example 2

630

530

25

2.49

Example 3

670

595

11

2.48

[0124] The microstructure characteristics of each embodiment are shown in Table 3.

[0125] The microstructural characteristics of each embodiment of table 3

[0126]

[0127]

[0128] Take embodiment 2 as an example to do component design:

[0129] Density estimate calculation:

[0130] Al content is 100% - (15.0% + 3.0% + 0.5% + 0.20%) = 81.3%;

[0131] The density of Al is 2.699g / cm 3 ;

[0132]...

Embodiment 2

[0136] Then embodiment 2 alloy density:

[0137] ρ=G / Σ(W i / ρ i )=100 / (15.0 / 1.74+3.0 / 2.34+0.5 / 7.4+0.20 / 4.54+81.3 / 2.699)=2.48g / cm 3

[0138] Example 2 Alloy Strength Prediction Calculation:

[0139] R m =35MPa / %×W j +100~300MPa≥625MPa.

[0140] Taking Example 2 as an example to do batching calculation: smelting 120kg.

[0141] 1) The chemical composition of Example 2 is as follows:

[0142] Mg: 15.0%; Si: 3.0%; Mn: 0.50%; Ti: 0.20%; Al: the balance is aluminum alloy and other unavoidable impurities.

[0143] 2) The amount of each alloy element required in the alloy is:

[0144] According to the charge of 120 kg of furnace charge, the ingredients are calculated, and the weight of the alloy elements that need to be added is:

[0145] Mg: 18.0 kg; Si: 3.6 kg; Mn: 0.6 kg; Ti: 0.24 kg; Al: the balance is 120 kg - the total algebraic sum of the above alloy elements (22.44 kg) is 97.56 kg.

[0146] 3) Because silicon and manganese are added in the form of intermediate alloy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

An aluminum alloy structural material, characterized in that: the aluminum alloy structural material is an Al-Mg-Si-Mn-Ti alloy, and the mass percentage of each element is: Mg: 10.5% to 17.4%, and contains Be: 0.01% ~0.05%, based on magnesium charge; Si: 1.0% ~ 5.0%; Mn: 0.3% ~ 0.8%; Ti: 0.15% ~ 0.25%; Al and other unavoidable impurities: the balance. When preparing, put the weighed charge into the intermediate frequency melting furnace for alloy melting, degassing and purification treatment, then pouring, spray deposition to make a round billet; then extrusion processing, finished product processing, and heat treatment are finished products . The formula design of the present invention is scientific and reasonable, the metallurgical structure of low-density high-strength aluminum alloy is prepared by spray deposition technology, the preparation process is simple and the process is short, and the prepared aluminum alloy has the mechanical properties of high-strength aluminum alloy and the low density of aluminum-lithium alloy. It can be used in the manufacture of ground vehicles and space vehicle structural products.

Description

technical field [0001] The invention belongs to the technical field of metal alloy materials and preparation, and in particular relates to a low-density and high-strength aluminum alloy structural material and a preparation method thereof, which are applicable to the manufacture of ground vehicles and space vehicle structural products. Background technique [0002] Pure aluminum has the characteristics of low density, good thermal conductivity, good plasticity and corrosion resistance. It is often used to make various profiles and plates. However, pure aluminum has poor strength and is not suitable for structural materials. Therefore, people add various materials to pure aluminum. A series of aluminum alloys are obtained by adding different alloying elements to strengthen the performance of aluminum. [0003] Nowadays, people improve the strength and density characteristics of aluminum alloy materials by adding low-density alloying elements such as magnesium, lithium, and si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/08C22C1/03C22C1/06C22F1/047
CPCC22C1/026C22C1/03C22C1/06C22C21/08C22F1/047
Inventor 孙廷富薛跃军彭银江陈耘郭安振崔崇亮郭峰翟景张涛元涛
Owner NO 52 INST OF CHINA NORTH IND GRP CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com