A glass wool self-release mesh belt

A self-release, glass wool technology, applied in the direction of layered products, metal layered products, synthetic resin layered products, etc., can solve the problem that the cotton felt structure is easily damaged, the mesh belt is difficult to clean, and the flame cotton felt mesh belt is entangled. problem, to achieve the effect of easy demoulding, clean production process and stable performance

Active Publication Date: 2017-08-18
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is intended to overcome the deficiencies in the prior art, to provide a glass wool self-demolding mesh belt, to overcome the existing glass wool felt products, especially the flame wool felt is easy to entangle with the mesh belt, the mesh belt is difficult to clean, and The problem that the structure of the prepared cotton felt is easily damaged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A glass wool self-release mesh belt
  • A glass wool self-release mesh belt
  • A glass wool self-release mesh belt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A glass wool self-demolding mesh belt, comprising a flexible surface layer, an intermediate support layer and a bottom layer, characterized in that the flexible surface layer is a composite membrane material with low surface energy, the intermediate support layer is a continuous mosaic structure of trapezoidal modules, and the bottom layer The thickness is 1mm, and the mesh belt is evenly distributed with circular holes with a radius of 0.5mm.

[0029] The thickness of the surface layer composite film is 100 μm, and it is formed by heat-compression composite of 10 μm thick polytetrafluoroethylene, 1 μm thick aluminum foil, 9 μm thick polyurethane, 50 μm thick polypropylene and 30 μm thick polyethylene.

[0030] The thickness of the middle layer is 2mm, wherein the length of the lower bottom of the trapezoidal module is 1cm, and the length of the upper bottom is 0.7cm. The trapezoidal modules are closely arranged side by side, and there are 2 rows of evenly distributed ci...

Embodiment 2

[0038] A glass wool self-demolding mesh belt, comprising a flexible surface layer, an intermediate support layer and a bottom layer, characterized in that the flexible surface layer is a composite membrane material with low surface energy, the intermediate support layer is a continuous mosaic structure of trapezoidal modules, and the bottom layer The thickness is 3mm, and the circular holes with a radius of 1mm are evenly distributed on the mesh belt.

[0039] The thickness of the surface layer composite film is 150 μm, which is composed of 20 μm thick polytetrafluoroethylene, 1.5 μm thick aluminum foil, 12 μm thick polyurethane, 80 μm thick polypropylene and 60 μm thick polyethylene.

[0040] The thickness of the middle layer is 6mm, wherein the length of the lower bottom of the trapezoidal module is 1.5cm, and the length of the upper bottom is 1cm. The trapezoidal modules are closely arranged side by side, and there are 5 rows of evenly distributed circular small holes on the...

Embodiment 3

[0048] A glass wool self-demolding mesh belt, comprising a flexible surface layer, an intermediate support layer and a bottom layer, characterized in that the flexible surface layer is a composite membrane material with low surface energy, the intermediate support layer is a continuous mosaic structure of trapezoidal modules, and the bottom layer The thickness is 5mm, and the circular holes with a radius of 2mm are evenly distributed on the mesh belt.

[0049] The thickness of the surface layer composite film is 250 μm, which is composed of 30 μm thick polytetrafluoroethylene, 2 μm thick aluminum foil, 18 μm thick polyurethane, 100 μm thick polypropylene and 100 μm thick polyethylene.

[0050] The thickness of the middle layer is 10mm, wherein the length of the lower bottom of the trapezoidal module is 2cm, and the length of the upper bottom is 1.4cm. The trapezoidal modules are closely arranged side by side, and there are 7 rows of uniformly distributed circular holes on the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A glass wool self-release mesh belt, comprising a flexible surface layer, an intermediate support layer and a bottom layer, characterized in that the flexible surface layer is a composite membrane material with low surface energy, the intermediate support layer is a continuous mosaic structure of trapezoidal modules, and the bottom layer The thickness is 1-5mm, and the mesh belt is evenly distributed with round holes with a radius of 0.5-2mm. The beneficial effects of the present invention are: ① easy demoulding; ② glass wool is not easily attached to the cotton-collecting mesh belt, so the production process is clean and hygienic; ③ glass wool products can be automatically separated from the mesh belt, and the glass wool products The structure and performance of the product will not be damaged, and the service life of the prepared product is longer and the performance is more stable.

Description

technical field [0001] The invention relates to a mesh belt structure, in particular to a glass wool self-release mesh belt. Background technique [0002] The technology of glass wool prepared by flame blowing method has been widely used in actual production since its formation. At present, glass wool products prepared by flame blowing method are widely used in the field of filtration, and the technology is also very mature. However, flame blowing Raw cotton products prepared by traditional methods are difficult to be prepared into felt-like products, which greatly limits the application form and stability of flame cotton, and causes great inconvenience to its application and promotion. [0003] The reason why it is difficult to prepare flame cotton products into felt products is mainly because the fiber diameter of glass wool products prepared by flame blowing method is thin and short, which is easy to cause the fibers to be entangled with the cotton-collecting mesh belt, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B7/12B32B3/24B32B15/06B32B15/08B32B15/18B32B15/20B32B25/08
Inventor 陈照峰吴操王伟伟李艳明杨勇叶信立沙李丽管胜男郑青
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS