Platinum metal recovery gauze during preparing process of nitric acid through ammoxidation
A technology for recovering net and platinum metal, applied in the direction of nitrogen oxides/oxyacids, nitric acid, process efficiency improvement, etc., can solve the problems of cracking and high cost of palladium, and achieve the effect of improving mechanical and physical properties and avoiding cracking phenomenon.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0010] Palladium with a purity of 99.5%, other elements by weight percentage Ni9%, Cu3%, Fe2%, Ag2%, Ce0.1%, brushed mesh, and the diameter of the recycled mesh is 0.1mm. The 3 layers of woven recycling mesh were placed under the catalytic mesh. After 180 days of normal operation, the recovery network was disassembled to recover the adsorbed platinum, and the measured actual recovery / actual loss was 0.54, so the recovery rate was 54%.
Embodiment 2
[0012] Palladium with a purity of 99.5%, other elements by weight percentage Ni10%, Cu3%, Fe2%, Ag1%, Ce00.2%, brushed mesh, and the diameter of the recycled mesh is 0.08mm. Place 6 layers of the woven recycling net under the catalytic net. After 180 days of normal operation, the recovery network was disassembled to recover the adsorbed platinum, and the measured actual recovery / actual loss was 0.62, so the recovery rate was 62%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap