Metal composite vacuum plate with edge sealed by seal strip and manufacturing method thereof

A metal composite and sealing strip technology, which is applied in climate change adaptation, insulation improvement, building components, etc., can solve problems such as cold bridges and thermal insulation performance not reaching the best state, so as to avoid damage, reduce temperature, and weld firmly Effect

Inactive Publication Date: 2015-07-01
戴长虹
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The patent applicant disclosed a series of vacuum panels and their production methods in July 2013, although they solved the problems of fire prevention, heat preservation and service life of existing thermal insulation materials However, since the metal plates are directly welded together, there are obvious cold bridges at the edges, making the thermal insulation performance not optimal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal composite vacuum plate with edge sealed by seal strip and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0043] Example: see figure 1 , the metal composite vacuum panel with sealing strip edge sealing is composed of a panel 1, a connecting layer 2, a vacuum chamber 3 and a support 4, and the panel 1 is composed of a thin metal plate such as a stainless steel plate or an aluminum alloy plate with a thickness of 0.2-1.5 mm; the connection Layer 2 is a high-temperature-resistant adhesive, which can be selected from high-temperature-resistant phenolic resin adhesives, epoxy resin adhesives, silicone resin adhesives, polyimide and other organic adhesives that can be cured at room temperature or high temperature, as well as commonly used inorganic adhesives or organic-inorganic composite adhesives, etc. ; The vacuum chamber 3 is welded by low-carbon steel plates with a thickness of 0.3-1.0mm; the support 4 is made of metal, ceramics, glass or high polymer, and is formed into a lattice by printing, printing, spraying, mechanical layout, etc. Distributed in the vacuum chamber 3, the supp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A metal composite vacuum plate with the edge sealed by a seal strip comprises a face plate, a connecting layer and a vacuum cavity and is characterized in that the face plate is a metal plate, the connecting layer enables the face plate and the vacuum cavity to be connected to form a whole, the face plate and / or the connecting layer provide / provides additional strength for the vacuum cavity and ensure / ensures the smoothness of the vacuum cavity under atmospheric pressure, the vacuum cavity is formed by welding a low-carbon steel plate in a vacuum furnace by utilizing a glass solder under the high vacuum and high temperature, the seal strip is arranged at the welding position of the edge portion of the low-carbon steel plate, the low-carbon steel plate is matched with the coefficient of thermal expansion of the glass solder, and a support is arranged in the vacuum cavity and is independently manufactured or is directly formed on the vacuum cavity. A manufacturing method of the metal composite vacuum plate is simple in process, the air impermeability of the vacuum cavity of the metal composite vacuum plate can be effectively ensured, the service life of the metal composite vacuum plate can be prolonged, and strength and heat-insulation, sound-insulation and fireproof performance can be improved.

Description

technical field [0001] The invention relates to the technical field of building energy conservation, in particular to a metal composite vacuum panel with edge sealing by sealing strips and a manufacturing method thereof. Background technique [0002] At present, the materials used for building exterior wall insulation are divided into A-grade thermal insulation materials and B-grade thermal insulation materials. A-grade thermal insulation materials have good fire resistance, but their thermal insulation performance and water resistance are lower than B-grade thermal insulation materials, and there are high prices. Complex construction technology and other issues; B-grade thermal insulation materials have the advantages of low cost, good thermal insulation performance, and mature construction technology, but their durability is not good, heat resistance is poor, and they are easy to burn. Moreover, it can accelerate the spread of fire, so it is forbidden to use organic therma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04B1/80C03C29/00E04B1/94
CPCY02A30/242Y02B80/10
Inventor 戴长虹
Owner 戴长虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products