A method and additive capable of accelerating clarification and impurity removal of potassium nitrate melt

A potassium nitrate and additive technology, applied in the direction of alkali metal nitrate purification, etc., can solve the problems of reducing the glass tempering effect and surface quality, increasing the cost of tempering, prolonging the clarifying time, etc., so as to shorten the clarifying time, speed up the clarifying, and improve the tempering effect. Effect

Active Publication Date: 2017-06-13
WUHAN UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the clarification time of potassium nitrate molten salt is not enough, the ammonium ions in it will not be completely volatilized, which will cause corrosion of the glass and reduce the tempering effect and surface quality of the glass.
If the clarification time is extended, the tempering cost will be greatly increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Select 100 parts by weight of industrial-grade first-class potassium nitrate salt with a purity of 99.7%. After the melting of potassium nitrate, add 1.5 parts by weight of potassium carbonate and 0.5 parts by weight of antimony trioxide and stir for 20 minutes; then add 0.2 parts by weight of silicon dioxide (phase α) and 0.2 parts by weight of aluminum oxide (phase β), and stir After uniformity, keep it warm at 460°C for 10 hours; use soda-lime-silica glass to temper at this temperature for 4 hours. After the tempering is completed, the surface stress of the glass is 511.2±7.0MPa, and the depth of the stress layer is 17.3±0.3μm, meeting the product requirements CSB-II-A specified in the JC / T977-2005 standard.

Embodiment 2

[0024] Select 100 parts by weight of industrial-grade first-class potassium nitrate salt with a purity of 99.7%. After the melting of potassium nitrate, add 1.5 parts by weight of potassium carbonate and 1.0 parts by weight of antimony trioxide and stir for 20 minutes; After homogeneity, keep it warm at 440°C for 10 hours; use soda-lime-silica glass to temper at this temperature for 4 hours. After the tempering is completed, the surface stress of the glass is 646.1±7.4MPa, and the depth of the stress layer is 12.4±0.1μm, meeting the product requirements CSB-III-A specified in the JC / T977-2005 standard.

Embodiment 3

[0026] Get 100 parts by weight of industrial-grade first-class potassium nitrate salt with a purity of 99.7%. After the melting of potassium nitrate, add 3 parts by weight of potassium carbonate and 2 parts by weight of antimony trioxide and stir for 20 minutes; then add 1 part by weight of silicon dioxide (phase α) and 1 part by weight of aluminum oxide (phase β), and stir After homogeneity, keep it warm at 450°C for 10 hours; use soda-lime-silica glass to temper at this temperature for 4 hours. After the tempering is completed, the surface stress of the glass is 586.7±6.2MPa, and the depth of the stress layer is 14.7±0.3μm, meeting the product requirements CSB-II-A specified in the JC / T977-2005 standard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface stressaaaaaaaaaa
depthaaaaaaaaaa
surface stressaaaaaaaaaa
Login to View More

Abstract

The invention provides a method capable of accelerating clarification and impurity removal of potassium nitrate melt, comprising the following steps: 1) selecting potassium nitrate, potassium carbonate, α-phase silicon dioxide, β-phase aluminum oxide and antimony trioxide; 2) Heating potassium nitrate above the melting temperature to melt potassium nitrate; 3) Adding potassium carbonate and antimony trioxide into molten potassium nitrate molten salt and stirring; 4) Mixing α-phase silicon dioxide and β-phase trioxide Dialuminum is added to the molten salt prepared in step 3), and stirred; 5) the above molten salt is kept warm and left to stand for more than 10 hours, and the tempering operation can be started after the solution is clarified. The additive of the present invention can quickly remove harmful impurities in potassium salt, effectively shorten the clarification time of potassium nitrate molten salt, reduce the concentration of harmful impurity ions in potassium nitrate molten salt, and improve the surface stress, stress layer depth and bending of chemically tempered glass strength and reduce production costs.

Description

technical field [0001] The invention relates to an additive, in particular to a method capable of accelerating the clarification and impurity removal of potassium nitrate melt and the additive. Background technique [0002] Chemical tempering (also known as ion exchange) can effectively increase the surface stress and bending strength of glass, and is one of the effective strengthening methods for thin glass and its products. In order to reduce the cost of chemical tempering, potassium nitrate of industrial grade purity is usually used. Potassium nitrate of industrial grade purity usually has more useless components and harmful impurity ions that reduce the effect of chemical toughening, such as ammonium ions, calcium ions, magnesium ions, etc. Industrial-grade potassium nitrate is mostly produced by ammonium nitrate conversion method, so potassium nitrate salt usually contains more ammonium ions. If the clarification time of potassium nitrate molten salt is not enough, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01D9/16
Inventor 刘超李晨蕊赵修建韩建军谢俊吕在国吕鑫张金奎蒋葵玲
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More