Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Rattan softening method

A rattan and treatment liquid technology, applied in the direction of reed/straw treatment, wood treatment, wood processing appliances, etc., can solve the problems of irrecoverable, cracked, broken rattan, etc., and achieves a simple softening method, enhanced corrosion resistance, and enhanced The effect of using performance

Inactive Publication Date: 2015-09-23
FUNAN TENGBO ARTS & CRAFTS CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rattan is relatively tough, if it is not softened, it will be difficult to weave. It will not only easily cause the rattan to crack or even break, resulting in an unattractive appearance of the product, but also reduce the firmness and corrosion resistance of the rattan product. Softening treatment method Softening treatment is carried out before weaving, but the effect of softening treatment is not ideal, and it cannot be recovered after softening, resulting in a decrease in the strength of rattan products during use, which affects normal use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rattan softening method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A kind of rattan softening method, comprises the following steps:

[0011] (1) Prepare treatment solution A, by weight, heat 180 parts of water, 7.6 parts of glycerin, 1.25 parts of pine nut oil, and 3.2 parts of castor oil to 35 ° C to make them fully mixed, then add 12.5 parts of urea and 4.2 parts of potassium nitrate , so that it is fully mixed and dissolved to obtain the treatment solution A;

[0012] (2) Soak the rattan in the treatment solution at 35-40°C for 15-20 hours, then remove the rattan and weave it;

[0013] (3) For the treatment of treatment solution B, add 3.8 parts of polyethylene glycol and 75 parts of water and stir at 42-45°C to fully dissolve it, then put the woven rattan products into it for soaking, and soak for 2 hours. Then add 3.5 parts of sodium bicarbonate to dissolve it, continue to soak for 3 hours, remove it, and rinse it with clean water.

[0014] Use the treatment solution A of the present invention to process, use 1000 rattans of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a rattan softening method. The method comprises the following steps that (1), treating fluid is prepared; (2), rattan is soaked in the treating fluid for 15 hours to 20 hours at the temperature of 35 DEG C to 40 DEG C, and then, the rattan is fished out to be woven; (3), treating fluid B is used for treating, 75 parts of water is added into 3.8 parts of polyethylene glycol, mixed fluid is stirred at the temperature of 42 DEG C to 45 DEG C, and is fully dissolved, then, the woven rattan product is put into the mixed fluid to be soaked for 2 hours, 3.5 parts of sodium bicarbonate is added into the mixed fluid to be dissolved, the rattan continues to be soaked for 3 hours, and then is fished out, and clean water is used for washing out the rattan. The rattan softening method is simple, the fluid A and the fluid B are used for treating respectively, and after the fluid A treats the rattan, the flexibility of the rattan is increased, and the phenomenon that in the weaving process, the rattan is broken down or cracked, and the quality of a product is decreased is avoided; and after weaving is completed, the fluid B is used for carrying out soaking treatment, the strength of the rattan is restored, and the use performance is increased.

Description

technical field [0001] The invention belongs to the field of wood treatment, and in particular relates to a rattan softening method. Background technique [0002] Rattan, a natural woven material. Also called "Teng Mie". A tough, extremely elongated vine. The outer skin of the rattan is smooth in color, smooth to the touch, and has excellent elasticity, which seems contemptuous but not contemptuous. It is also commonly used to weave rattan chairs, rattan boxes and other daily utensils. Rattan is relatively tough, if it is not softened, it will be difficult to weave. It will not only easily cause the rattan to crack or even break, resulting in an unattractive appearance of the product, but also reduce the firmness and corrosion resistance of the rattan product. The softening treatment method is to carry out softening treatment before weaving, but the softening treatment effect is not ideal, and it cannot be recovered after softening, resulting in a decrease in the strengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K5/06B27K3/02B27K3/52
CPCB27K9/002B27K3/52
Inventor 腾博
Owner FUNAN TENGBO ARTS & CRAFTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com