A technology of lost foam casting and hammer head, which is applied in the field of lost foam casting hammer head, which can solve the problems that it is difficult to guarantee the wear resistance and strength requirements of the hammer head, and achieve the effects of superior wear resistance, long service life and improved hardness
Inactive Publication Date: 2015-09-30
LIUZHOU JINTE NEW WEAR RESISTANT MATERIAL CO LTD
View PDF5 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, it is difficult to ensure the wear resistance and strength requi
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] A lost foam casting hammer, comprising the following chemical composition, by weight percentage:
[0013] C 3.8%, Si 1.1%, Mn 1.2%, Cr 12.0%, Mo 0.35%, Cu 0.12%, V 0.12%, Nb 0.018%, Ti 0.04%, W 0.04%, B 0.04%, Ce 0.06%, the rest are Fe.
Embodiment 2
[0015] A lost foam casting hammer, comprising the following chemical composition, by weight percentage:
[0016] C 3.2%, Si 1.4%, Mn 1.0%, Cr 12.8%, Mo 0.31%, Cu 0.14%, V 0.07%, Nb 0.020%, Ti 0.03%, W 0.05%, B 0.02%, Ce 0.08%, and the rest Fe.
Embodiment 3
[0018] A lost foam casting hammer, comprising the following chemical composition, by weight percentage:
[0019] C 4%, Si 0.9%, Mn 1.5%, Cr 11.4%, Mo 0.36%, Cu 0.08%, V 0.16%, Nb 0.010%, Ti 0.045%, W 0.02%, B 0.05%, Ce 0.05%, and the rest Fe.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an evanescent mode casting hammerhead which comprises the following chemical components by weight percent: 3.2%-4% of C, 0.9%-1.4% of Si, 1.0%-1.5% Mn, 11.4%-12.8% Cr, 0.31%-0.36% of Mo, 0.08%-0.14% of Cu, 0.07%-0.16% of V, 0.010%-0.020% of Nb, 0.03%-0.045% of Ti, 0.02%-0.05% of W, 0.02%-0.05% of B, 0.05%-0.08% of Ce, and the balance being Fe. According to the evanescent mode casting hammerhead of a high-strength crusher, on the basis of a high-chromium alloy, a manganese element is additionally added, so that the hardness is improved effectively, the wear-resisting property is more superior than those of a hard alloy hammerhead and a high-chromium alloy hammerhead at present, and the service life is longer.
Description
technical field [0001] The invention relates to a lost foam casting hammer head. Background technique [0002] Lost foam casting is a new technology with almost no margin and precise molding. This process does not require mold taking, no parting surface, and no sand core. Dimensional errors caused by combination. The surface roughness of the casting can reach Ra3.2 to 12.5μm; the dimensional accuracy of the casting can reach CT7 to 9; the machining allowance is at most 1.5 to 2mm, which can greatly reduce the cost of machining, compared with the traditional sand casting method, it can reduce 40 % to 50% of the machining volume. However, it is difficult to guarantee the required wear resistance and strength requirements of the hammer head by using the lost foam casting hammer head. Contents of the invention [0003] The technical problem to be solved by the invention is to overcome the existing defects and provide a lost foam casting hammer head made of high chromium and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): C22C38/36
Inventor 何拥军蒋漓洪伍斌华杨学赖卫华黄立德梁英豪
Owner LIUZHOU JINTE NEW WEAR RESISTANT MATERIAL CO LTD