A kind of gel memory foam and preparation method thereof

A technology of memory foam and gel, which is applied in the field of gel memory foam and its preparation, can solve problems such as the decline of slow rebound ability, and achieve the effects of comprehensive performance improvement, product market competitiveness, and improved heat transfer capacity

Active Publication Date: 2017-10-03
佛山市惠安家居用品有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies in the prior art, the present invention is to provide a gel memory foam and its preparation method, aiming to solve the problem that the existing gel memory foam improves its heat transfer ability and its own characteristics and slow rebound ability decrease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] The gel memory foam is made from the following raw materials in parts by weight:

[0065] Slow rebound polyether polyol 60 parts;

[0066] 25 parts of soft foam polyether polyol;

[0067] 15 parts of polymer polyols;

[0068] 5 parts of silica gel powder;

[0069] 35 parts of toluene diisocyanate;

[0070] 1.56 parts of water;

[0071] Silicone oil 8002 1 part;

[0072] A-33 0.3 copies;

[0073] T-9 0.1 part;

[0074] 2 parts of opening agent.

[0075] The fineness of the silica gel powder is 60 meshes, the hydroxyl value of the slow rebound polyether polyol is 300 mgKOH / g, the hydroxyl value of the soft foam polyether polyol is 50 mgKOH / g, and its molecular weight is 3000. The molecular weight of the elastic polyether polyol is 550, and the hydroxyl value of the polymer polyol is 30 mgKOH / g.

[0076] Prepare slow rebound gel memory foam based on the above formula, and its preparation steps are as follows:

[0077] Slowly rebound polyether polyol, soft foam poly...

Embodiment 2

[0080] The gel memory foam is made from the following raw materials in parts by weight:

[0081] Slow rebound polyether polyol 55 parts;

[0082] 30 parts of soft foam polyether polyol;

[0083] 15 parts of polymer polyols;

[0084] 5 parts of silica gel powder;

[0085] 40 parts of toluene diisocyanate;

[0086] 1.56 parts of water;

[0087] Silicone oil 8002 1 part;

[0088] A-33 0.3 copies;

[0089] T-9 0.1 part;

[0090] 2 parts of opening agent.

[0091] The fineness of the silica gel powder is 80 meshes, the hydroxyl value of the slow rebound polyether polyol is 220 mgKOH / g, the hydroxyl value of the soft foam polyether polyol is 48 mgKOH / g, and its molecular weight is 3000. The molecular weight of the elastic polyether polyol is 550, and the hydroxyl value of the polymer polyol is 25 mgKOH / g.

[0092] Prepare slow rebound gel memory foam based on the above formula, and its preparation steps are as follows:

[0093] Slow rebound polyether polyol, soft foam poly...

Embodiment 3

[0096] The gel memory foam is made from the following raw materials in parts by weight:

[0097] Slow rebound polyether polyol 60 parts;

[0098] 30 parts of soft foam polyether polyol;

[0099] 20 parts of polymer polyols;

[0100] 5 parts of silica gel powder;

[0101] 30 parts of toluene diisocyanate;

[0102] 1.56 parts of water;

[0103] Silicone oil 8002 1 part;

[0104] A-33 0.3 copies;

[0105] T-9 0.1 part;

[0106] 2 parts of opening agent.

[0107] The fineness of the silica gel powder is 50 mesh, the hydroxyl value of the slow rebound polyether polyol is 280 mgKOH / g, the hydroxyl value of the soft foam polyether polyol is 56 mgKOH / g, and its molecular weight is 3000. The molecular weight of polyether polyol is 550, and the hydroxyl value of polymer polyol is 28 mgKOH / g

[0108] Prepare slow rebound gel memory foam based on the above formula, and its preparation steps are as follows:

[0109] A. Mix slow rebound polyether polyol, soft foam polyether polyol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention provides gel remembering sponge and a preparation method thereof. The gel remembering sponge is formed by mixing and foaming the following raw materials by weight: 55 to 65 parts of slow rebound polyether polyol, 20 to 30 parts of soft-foam polyether polyol, 10 to 20 parts of polymer polyol, 5 parts of silica-gel powder, and 30 to 40 parts of toluene diisocyanate. The gel remembering sponge adopts an original sponge formula, so as to greatly improve the heat-transfer capability of the gel remembering sponge, and ensure that a person can feel cool when being in touch with the gel remembering sponge, the original slow rebound resilience of the gel remembering sponge is not reduced, and the comprehensive performance of the gel remembering sponge is improved finally. Therefore, the market competitiveness of the gel remembering sponge is obviously higher than those of the conventional like products.

Description

technical field [0001] The invention relates to the technical field of sponge products, in particular to a gel memory sponge and a preparation method thereof. Background technique [0002] Sponge products are widely used in furniture products, and gel memory foam with slow rebound effect is used as filling material in middle and high-end furniture. However, the current sponge products have the problem of poor heat transfer effect, which makes filling Sponge furniture is not suitable for use in hot summer weather, which also affects the popularity of furniture filled with sponge materials. At present, the improvement of the heat transfer effect of sponge products will cause a serious loss of the characteristics of the sponge product itself, such as gel memory foam. It is said that while its heat transfer ability is improved, its slow rebound effect and the characteristics of the sponge itself will be destroyed, thus affecting product performance. [0003] Therefore, prior ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/48C08G18/40C08J9/08C08G101/00
CPCC08G18/4009C08G18/4804C08G2220/00C08G2110/0083
Inventor 邓纳新
Owner 佛山市惠安家居用品有限公司