High-strength ABS pipe fitting

A high-strength ABS resin technology, applied in the field of composite materials, can solve the problems of large consumption of ABS resin, impact on enterprise cost, poor impact resistance, etc., and achieve the effects of anti-aging, low cost, and good sound insulation effect

Inactive Publication Date: 2015-11-11
刘民钦
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing ABS pipe production consumes a large amount of ABS resin, which has a great impact on the cost of the enterprise. Therefore, it is the current research to study an ideal substitute that can reduce the amount of ABS resin used and has no impact on the output of ABS pipes. Hotspots
Pipes made of ABS materials are widely used because of their light weight, low cost and good corrosion resistance, but their disadvantages are that their toughness is poor at low temperatures, and their impact resistance decreases as the temperature decreases. Worse, easily broken when impacted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A high-strength ABS pipe includes raw materials in the following weight ratios: 80 parts of ABS resin, 25 parts of polyacrylate, 5 parts of calcium-zinc composite stabilizer, 4 parts of ACR foaming agent, and 3 parts of MB anti-aging agent.

Embodiment 2

[0019] A high-strength ABS pipe, including the following raw materials in weight ratio: 70 parts of ABS resin, 20 parts of polyacrylate, 6 parts of calcium-zinc composite stabilizer, 4 parts of ACR foaming agent, and 5 parts of MB anti-aging agent.

Embodiment 3

[0021] A high-strength ABS pipe includes raw materials in the following weight ratios: 90 parts of ABS resin, 23 parts of polyacrylate, 4 parts of calcium-zinc composite stabilizer, 3 parts of ACR foaming agent, and 4 parts of MB anti-aging agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of a composite material, in particular to a high-strength ABS pipe fitting. The pipe fitting comprises the following raw materials in part by weight: 60 parts of ABS resin, 26 parts of polyacrylate, 7 parts of stabilizer, 5 parts of foaming agent and 2 parts of anti-aging agent. The ABS pipe fitting can effectively prevent the aging, and is high in flexibility, high in elongation rate, high in impact-resisting strength and tensile strength at a normal temperature, lighter in weight, resistant to pressure and impact and better in sound-insulation effect.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a high-strength ABS pipe. Background technique [0002] The existing ABS pipe production consumes a large amount of ABS resin, which has a great impact on the cost of the enterprise. Therefore, it is the current research to study an ideal substitute that can reduce the amount of ABS resin used and has no impact on the output of ABS pipes. hotspots. Pipes made of ABS materials are widely used because of their light weight, low cost and good corrosion resistance, but their disadvantages are that their toughness is poor at low temperatures, and their impact resistance decreases as the temperature decreases. It is getting worse and worse, and it is extremely fragile when it is impacted. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention provides a high-strength ABS pipe. . [0004] Scheme of the present invention is achieved by: [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L33/04C08K5/37C08J9/08
Inventor 刘民钦
Owner 刘民钦