Chemical resistant superhydrophilic and underwater superoleophobic oil-water separation membrane and its preparation and application

A super oleophobic oil and chemical resistance technology, applied in the field of oil-water separation membrane preparation, can solve the problems of poor performance, poor water resistance and chemical resistance, achieve fast speed, good chemical resistance, and expand the scope of use Effect

Active Publication Date: 2017-06-16
SOUTH CHINA AGRI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The Chinese invention patents with authorized patent numbers ZL 2013 1 0240149.1 and ZL 2013 1 0224027.4 have invented a UV-curable superhydrophilic and underwater superoleophobic oil-water separation membrane with a hydrophilic polymer molecular brush structure and a thermally cured water separation membrane. Gel structure superhydrophilic and underwater superoleophobic oil-water separation membranes have good oil-water separation effect and oil pollution resistance, but the water resistance and chemical resistance of the membrane are poor
The Chinese invention patent with the authorized patent number ZL 2013 1 0241229.4 invented a graphene oxide modified super-hydrophilic and underwater super-oleophobic oil-water separation membrane. Water resistance and chemical resistance performance, but its performance is still far from the effect of the present invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemical resistant superhydrophilic and underwater superoleophobic oil-water separation membrane and its preparation and application
  • Chemical resistant superhydrophilic and underwater superoleophobic oil-water separation membrane and its preparation and application
  • Chemical resistant superhydrophilic and underwater superoleophobic oil-water separation membrane and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] (1) Put a piece of 15×15mm 2 The 300-mesh stainless steel wire mesh was immersed in distilled water, ethanol or acetone, and distilled water in order, respectively, and ultrasonically cleaned at 150W and 40KHz for 8min, and hung up to dry at room temperature.

[0058] (2) Add 50g of tetraethoxysilane, 100g of absolute ethanol and 20g of deionized water into a four-neck flask, heat in a constant temperature water bath at 35°C and keep stirring. After stirring evenly, weigh 0.5g of 25% Add ammonia water to 30g of deionized water, drop it into a four-necked flask at a rate of 1mL / min with a constant flow pump, keep warm for 4 hours, and discharge to prepare a nano-silica sol with a particle size of about 10nm, with a mass content of nanoparticles of 20%. The structure of the synthesized nanoparticles was tested by a Fourier transform infrared tester. figure 1 The infrared spectrum is visible at 3400cm -1 There is a strong absorption peak at , which is the absorption peak...

Embodiment 2

[0067] (1) Put a piece of 15×15mm 2 The 100-mesh copper wire mesh was immersed in distilled water, ethanol, and distilled water in order, respectively, and was cleaned at 100W and 20KHz for 10min, and hung up to dry at room temperature.

[0068] (2) Add 50g of tetramethoxysilane, 100g of absolute ethanol and 20g of deionized water into a four-necked flask, heat it in a constant temperature water bath at 80°C and keep stirring. After stirring evenly, weigh 0.5g of 25% Add hydrochloric acid to 30 g of deionized water, drop it into a four-necked flask at a rate of 1 mL / min with a constant flow pump, and discharge after 4 hours of heat preservation to prepare a nano-silica sol with a particle size of 500 nm and a mass content of nanoparticles of 35%. The structure of the synthesized nanoparticles was tested by a Fourier transform infrared tester, and the obtained structure diagram was consistent with that of figure 1 resemblance.

[0069] (3) Dilute the UV-curable epoxy acrylate...

Embodiment 3

[0075] (1) Put a piece of 15×15mm 2 The 200-mesh aluminum wire mesh was immersed in distilled water, ethanol or acetone, and distilled water in order, respectively, and ultrasonically cleaned at 150W and 40KHz for 10min, and hung up to dry at room temperature.

[0076](2) Add 50g of tetramethoxysilane, 100g of absolute ethanol, and 20g of deionized water into a four-neck flask, heat in a constant temperature water bath at 35°C and keep stirring. After stirring evenly, weigh 0.5g of 25% Add sodium bicarbonate to 30g of deionized water, drop it into a four-necked flask with a constant flow pump at a rate of 1.5mL / min, and discharge after 5 hours of heat preservation to prepare a nano-silica sol with a particle size of 200nm, and the mass content of the nanoparticles is 35%. . The structure of the synthesized nanoparticles was tested by a Fourier transform infrared tester, and the obtained structure diagram was consistent with that of figure 1 resemblance.

[0077] (3) Dilute ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of oil-water separation membrane preparation, and discloses a chemical-resistant super-hydrophilic and underwater super-oleophobic oil-water separation membrane, a preparation method and application thereof. The oil-water separation membrane is prepared by the following method: first prepare the nano sol, and then mix it with a monofunctional UV curable oligomer, a bifunctional UV curable oligomer, and a multifunctional UV curable oligomer to obtain a UV curable water-based coating; Apply UV curable water-based anti-corrosion coating on the surface of the screen by coating or spraying method, after drying, UV-cured to obtain an anti-corrosion primer coating film; then apply the above UV-curable water-based coating to the obtained anti-corrosion The surface of the omentum is primed, dried, and UV-cured to obtain a chemical-resistant super-hydrophilic and underwater super-oleophobic oil-water separation membrane. The separation membrane of the invention has a contact angle of 0° to water and oil in air, and a contact angle of more than 150° to oil droplets underwater, and can be applied to the separation of oil-water mixture and the treatment of oily sewage.

Description

technical field [0001] The invention belongs to the technical field of preparation of oil-water separation membranes, in particular to a chemical-resistant super-hydrophilic and underwater super-oleophobic oil-water separation membrane and its preparation method and application. Background technique [0002] In recent years, the research on macromolecular self-assembly has made a series of significant progress, which has become a research hotspot. One of the important application areas is molecular brush polymers, which have good application prospects in self-cleaning, antifouling coatings and other fields. . When the surface of the membrane has a hydrophilic polymer molecular brush structure, the surface hydrophilicity of the membrane will be better. At the same time, because the hydrophilic polymer molecular brush is in a fully extended structure in water, the surface of the membrane has a On the basis of the binary rough structure, there is also a nano-scale fluff struct...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/06B01D69/02B01D67/00B01D17/022
Inventor 袁腾杨卓鸿涂伟萍周显宏
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap