Polyamide 6 composite and preparation method thereof

A composite material and polyamide technology, applied in the field of materials, can solve problems such as poor fluidity, and achieve the effects of improving appearance, reducing warpage and deformation, and maintaining length

Inactive Publication Date: 2015-12-16
NANJING JULONG SCI&TECH CO LTD
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is: in view of the shortcomings of the above technologies, a polyamide 6 composite material and its preparation method are proposed, which solves the problem of poor fluidity of the material, and makes the injection molded product of the composite material have better Comprehensive performance and good appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyamide 6 composite and preparation method thereof
  • Polyamide 6 composite and preparation method thereof
  • Polyamide 6 composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A polyamide 6 composite material, each raw material comprises the following parts by weight: polyamide 6: 87.6 parts, alkali-free chopped glass fiber: 5 parts, mica: 2 parts, maleic anhydride grafted polyethylene: 3 parts, titanium Ester coupling agent: 0.1 part, antioxidant: 0.6 part, hypophosphite: 0.1 part, black masterbatch is a mixture of polyethylene carrier inorganic black masterbatch and polyamide 6 carrier organic black masterbatch, wherein polyethylene carrier inorganic black masterbatch 0.5 parts, polyamide 6 carrier organic black masterbatch 0.5 parts, stearic acid amide: 0.6 parts.

[0036] The relative viscosity of polyamide 6 is 2.8; the fiber diameter of alkali-free chopped glass fiber is 13 μm, and the fiber length is 4.5 mm; the particle size of mica is 80 μm; the antioxidant is compounded with 1098 and 168, and the weight ratio is 1:1 .

[0037] A kind of preparation method of polyamide 6 composite material comprises the following steps:

[0038] St...

Embodiment 2

[0042] A polyamide 6 composite material, each raw material comprises the following parts by weight: polyamide 6: 82.6 parts, alkali-free chopped glass fiber: 10 parts, calcium carbonate: 2 parts, maleic anhydride grafted EPDM: 3 parts, aluminum Ester coupling agent: 0.1 part, antioxidant: 0.6 part, hypophosphite: 0.1 part, black masterbatch is a mixture of polyethylene carrier inorganic black masterbatch and polyamide 6 carrier organic black masterbatch, wherein polyethylene carrier inorganic black masterbatch 0.5 parts, polyamide 6 carrier organic black masterbatch 0.5 parts; stearic acid amide: 0.6 parts.

[0043] The relative viscosity of polyamide 6 is 2.8; the fiber diameter of alkali-free chopped glass fiber is 13 μm, and the fiber length is 4.0 mm; the particle size of calcium carbonate is 40 μm; the antioxidant is compounded with 1098 and 168, and the weight ratio is 1:1.

[0044] A kind of preparation method of polyamide 6 composite material comprises the following st...

Embodiment 3

[0050] A polyamide 6 composite material, each raw material comprises the following parts by weight: polyamide 6: 80.2 parts, alkali-free chopped glass fiber: 10 parts, talcum powder: 5 parts, maleic anhydride grafted EPDM 3 parts, silane coupling Agent KH560: 0.1 parts, antioxidant: 0.4 parts, hypophosphite: 0.1 parts, black masterbatch is a mixture of inorganic carrier-free black masterbatch and polyamide 6 carrier organic black masterbatch, of which inorganic carrier-free black masterbatch 0.2 parts, polyamide 6 Carrier organic black masterbatch: 0.4 parts; silicone: 0.6 parts.

[0051] The relative viscosity of polyamide 6 is 2.8; the alkali-free chopped glass fiber has a fiber diameter of 13 μm and a fiber length of 4.0 mm; the particle size of talc powder is 10 μm; the antioxidant is a compound of 1098 and 168, and the weight ratio is 1:1 .

[0052] A kind of preparation method of polyamide 6 composite material comprises the following steps:

[0053] Step 1, mineral tre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite and a preparation method thereof, in particular to a polyamide 6 composite and a preparation method thereof. Non-alkali chopped fibers are selected to serve as a reinforcing agent of the pyamide 6 composite, and compatilizer is added to improve fatigue durability and low-temperature brittleness of glass fiber reinforcing materials. Coupling reagents, lubricating agents and inorganic minerals are added to improve the combination of the polyamide 6 composite and the glass fibers, and dispersion of the glass fibers in the polyamide 6 composite is enhanced, so that the glass fibers are not prone to being exposed outside the surface, and a good surface is achieved. The polyamide 6 composite and the eparation method thereof have the advantages that the polyamide 6 composite can be used for injection molding of automobile doors and window frame decoration strips.

Description

technical field [0001] The invention belongs to the technical field of materials, and relates to a composite material and a preparation method thereof, in particular to a polyamide 6 composite material and a preparation method thereof. Background technique [0002] In the automotive industry, the components involving polyamide 6 in its structure or decoration have become a highly concentrated area of ​​research and development. In addition, the market has higher and higher requirements for injection molding grade polyamide 6 materials, and the development of this field is becoming more and more rapid. . [0003] As we all know, polyamide 6 has good comprehensive properties, low density, easy molding, large design freedom, heat insulation, and has obvious advantages in mold and assembly costs. Polyamide 6 not only has high tensile strength, excellent impact performance, but also has high heat distortion temperature, heat resistance, low friction coefficient, wear resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L51/06C08L23/06C08K13/04C08K7/14C08K3/34C08K3/32C08K5/20C08K3/26C08L51/04C08L83/04C08K7/20
CPCC08L77/02C08K2201/003C08K2201/004C08L2205/03C08L2205/24C08L51/06C08L23/06C08K13/04C08K7/14C08K3/34C08K3/32C08K5/20C08L51/04C08K2003/265C08L83/04C08K7/20
Inventor 薛建峰周勇吴汾张圣国
Owner NANJING JULONG SCI&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com