Red concrete block and preparation method thereof

A concrete block and red technology, which is applied in the field of building materials, can solve the problems of self-weight and thermal insulation performance that cannot meet the needs of building energy conservation, and achieve the effects of bright color, lower production costs, and light weight

Inactive Publication Date: 2016-01-20
嘉善远大新型墙体有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current concrete blocks generally use ordinary pigments, and their self-weight and thermal insulation properties cannot meet the needs of buildings for building energy conservation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A kind of red concrete block, this block is made up of following material by weight:

[0059] 65 parts of white cement

[0060] Iron tailings 35 parts

[0061] 35 parts of fly ash

[0062] 35 parts of gravel

[0063] Calcium aluminum silicate 15 parts

[0064] 15 parts of hydroxyethyl methylcellulose ether

[0065] Basalt fiber 15 parts

[0066] 15 parts of redispersible latex powder

[0067] 15 parts of mineral wool slag

[0068] Naphthalene-based high-efficiency water reducer 5 parts

[0069] 5 parts of chromium yttrium aluminum red ceramic

[0070] Sodium thiosulfate 5 parts

[0071] 5 parts of red mud

[0072] Composite additive 4 parts.

[0073] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0074] Described composite additive is made up of the material of following parts by weight:

[0075] 9 parts spodumene

[0076] Phosphogypsum 9 parts

[0077] Silica powder 9 parts

[007...

Embodiment 2

[0084] A kind of red concrete block, this block is made up of following material by weight:

[0085] 60 parts of white cement

[0086] Iron tailings 30 parts

[0087] 30 parts of fly ash

[0088] 30 parts of gravel

[0089] Calcium aluminum silicate 10 parts

[0090] 10 parts of hydroxyethyl methylcellulose ether

[0091] Basalt fiber 10 parts

[0092] 10 parts of redispersible latex powder

[0093] 10 parts mineral wool slag

[0094] Naphthalene superplasticizer 2 parts

[0095] Chromium yttrium aluminum red ceramic 2 parts

[0096] Sodium thiosulfate 2 parts

[0097] 2 parts red mud

[0098] 2 parts of compound additives.

[0099] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0100] Described composite additive is made up of the material of following parts by weight:

[0101] 9 parts spodumene

[0102] Phosphogypsum 9 parts

[0103] Silica powder 9 parts

[0104] 9 parts of fumed aluminu...

Embodiment 3

[0110] A kind of red concrete block, this block is made up of following material by weight:

[0111] 70 parts of white cement

[0112] 40 parts of iron tailings

[0113] 40 parts of fly ash

[0114] 35 parts of gravel

[0115] Calcium aluminum silicate 20 parts

[0116] 15 parts of hydroxyethyl methylcellulose ether

[0117] Basalt fiber 15 parts

[0118] 20 parts of redispersible latex powder

[0119] 15 parts of mineral wool slag

[0120] Naphthalene-based high-efficiency water reducer 5 parts

[0121] 5 parts of chromium yttrium aluminum red ceramic

[0122] 1 part sodium thiosulfate

[0123] 1 part red mud

[0124] Composite additive 4 parts.

[0125] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0126] Described composite additive is made up of the material of following parts by weight:

[0127] Spodumene 6 parts

[0128] Phosphogypsum 6 parts

[0129] Silica powder 9 parts

[0130]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a red concrete block and a preparation method thereof. The block comprises white cement, iron tailings, fly ash, gravel, calcium aluminum silicate, hydroxyethyl methyl cellulose ether, basalt fibers, redispersible latex powder, mineral wool slag, a naphthalene-based superplasticizer, chromium-yttrium-aluminum red ceramic, sodium thiosulfate, red mud and a composite additive. Various raw materials of the concrete block are creatively and organically combined, and the red concrete block with good compression resistance, fire-proofing, heat insulation, health care, environmental protection, small heat-conducting coefficient, light weight, low water absorption and bright color is obtained with an optimized preparation process.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a red concrete block and a preparation method thereof. Background technique [0002] With the rapid development of my country's building ceramics industry, my country's demand for building ceramic materials is becoming more and more vigorous, and at the same time, the requirements for various performances of building materials are getting higher and higher. It is more and more common to use concrete decorative blocks for the walls of residential quarters, roofs and floors of buildings, square walls, and protective slope embankments. Especially the research of colored blocks is a direction of research now. However, the current concrete blocks generally use ordinary pigments, and their self-weight and thermal insulation properties cannot meet the needs of buildings for building energy conservation. Contents of the invention [0003] The purpose of the pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/00C04B18/14C04B22/14
CPCY02W30/91
Inventor 王建国
Owner 嘉善远大新型墙体有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap