Method for separating tellurium in crude selenium refining process

A refining process, crude selenium technology, applied in the field of metallurgy, can solve the problems such as the quality of refined selenium powder cannot meet the requirements, the effect of impurity removal is not good, etc., achieve good promotion value and economic benefits, shorten the production cycle, and optimize the process

Active Publication Date: 2016-01-27
JINCHUAN GROUP LIMITED
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for separating tellurium in the complex crude selenium refining process with high tellurium content, so as to solve the problem of poor impurity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for separating tellurium in crude selenium refining process
  • Method for separating tellurium in crude selenium refining process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for separating tellurium in the refining process of high tellurium-containing complex crude selenium (alloy crude selenium), wherein the mass percentage content of tellurium as an impurity in the crude selenium is 3.56%, which comprises the following steps:

[0022] Step 1, weigh the 45% sodium carbonate powder of the impurity tellurium quality contained in the coarse selenium, add in the oxidation furnace after the sodium carbonate powder is uniformly mixed with the coarse selenium;

[0023] Step 2. Heating the oxidation furnace. When the temperature of the furnace rises to 100°C, feed oxygen, and the flow rate of oxygen is controlled at 15Nm 3 / h, when the temperature rises to 500°C, increase the oxygen flow rate to 25Nm 3 / h, the pressure in the oxidation furnace is -29Mpa, and at the same time replenish water in the absorption tank of the oxidation furnace in time to ensure that the negative pressure in the furnace is stable. The feeding time is 4.21h, the...

Embodiment 2

[0026] A method for separating tellurium during the refining process of high-tellurium-containing complex crude selenium (selenium material obtained by leaching of alloy blowing acid mud), wherein the mass percentage content of tellurium as an impurity in the crude selenium is 8.11%, which includes the following steps:

[0027] Step 1, weigh the 55% sodium carbonate powder of impurity tellurium quality contained in the coarse selenium, add in the oxidation furnace after the sodium carbonate powder is evenly mixed with the coarse selenium;

[0028] Step 2: Heating the oxidation furnace. When the temperature of the furnace rises to 100°C, feed oxygen, and the flow rate of oxygen is controlled at 20Nm 3 / h, when the temperature rises to 500°C, increase the oxygen flow rate to 25Nm 3 / h, the pressure in the oxidation furnace is -30Mpa, and at the same time replenish water in the absorption tank of the oxidation furnace in time to ensure that the negative pressure in the furnace is...

Embodiment 3

[0032] A method for separating tellurium in the refining process of high-tellurium-containing complex crude selenium (sedimented selenium slag), wherein the mass percent content of tellurium as an impurity in the crude selenium is 5.11%, which comprises the following steps:

[0033] Step 1, weighing 50% sodium carbonate powder of the impurity tellurium quality contained in the coarse selenium, adding the sodium carbonate powder and coarse selenium into the oxidation furnace after being uniformly mixed;

[0034] Step 2: The oxidation furnace is heated. When the temperature of the furnace rises to 100°C, the oxygen flow rate is controlled at 18Nm3 / h. When the temperature rises to 500°C, the oxygen flow rate is increased to 25Nm3 / h. The pressure is -32Mpa. At the same time, water is replenished in the absorption tank of the oxidation furnace in time to ensure a stable negative pressure in the furnace. The temperature in the first section of the oxidation furnace is controlled to b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of metallurgy, and particularly relates to a method for separating tellurium in the high tellurium containing complex crude selenium refining process. A certain amount of sodium carbonate is added to crude selenium, selenium and tellurium both can react with sodium carbonate to generate corresponding salt in the oxidation process, selenium salt is heated to be fast decomposed and volatilized at certain temperature, and generates corresponding selenium dioxide with oxygen, selenium dioxide is absorbed by water to generate a seleninic acid solution, and tellurium salt is not likely to volatilize and is mostly enriched in oxidizing slag. The oxidizing temperature of one segment of an oxidizing furnace is increased, tellurium and selenium are fully separated, the acidity of the seleninic acid solution is improved through sulfuric acid before reduction, the reduction rate of SO2 on tellurium is lowered, tellurium in the seleninic acid solution is left in the solution as much as possible, and therefore selenium and tellurium are further separated, and the quality of fine selenium powder is ensured. According to the method, the process of an oxygen oxidation method is optimized, the production period is shortened, the quantity of reagents is reduced, production cost is reduced, the direct recovery rate of selenium is improved to 94% from original 92.6%, and good popularization value and economic benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and specifically relates to a method for separating tellurium in a complex crude selenium refining process with high tellurium content, which can effectively realize the purification of crude selenium materials with high tellurium impurities. Background technique [0002] Oxygen oxidation is the best refining process for crude selenium (grade 94-98%, tellurium content 0.005%) produced by rotary kiln sulphation and roasting, which was successfully developed in China in the late 1970s and has been used in practice for a long time. The process has the advantages of short process, low cost, high yield and simple operation. However, with the transformation of the copper anode slime treatment process, the grade and impurities of crude selenium produced are also different, such as the precipitated selenium slag (85% grade, 2-7% tellurium content) obtained by pressure leaching of copper anode slime, p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B19/02
Inventor 宋宏儒王军洪渊陈云峰吴建明
Owner JINCHUAN GROUP LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com