Phase change graphite heat conduction material with high thermal conductivity and preparation method

A technology of graphite heat conduction and heat conduction materials, which is applied in the direction of heat exchange materials, chemical instruments and methods, etc., can solve problems such as inability to meet heat dissipation requirements, and achieve excellent interface heat conduction effects, excellent wetting effects, and good storage stability.

Inactive Publication Date: 2016-02-24
SHENZHEN DARBOND INTERFACE MATERIALS
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the fact that most of the existing thermal interface materials cannot meet the current

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phase change graphite heat conduction material with high thermal conductivity and preparation method
  • Phase change graphite heat conduction material with high thermal conductivity and preparation method
  • Phase change graphite heat conduction material with high thermal conductivity and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] The components and contents of phase change thermal conductive materials are as follows:

[0023]

[0024] Specific preparation method:

[0025] Add fully refined No. 58 paraffin, antioxidant 1076, coupling agent γ-methacryloxypropyltrimethoxysilane in the planetary power mixer according to the formula ratio, raise the temperature to 70 degrees Celsius, and stir for 45 Minutes into a uniform paste;

[0026] Then add the cross-linking agent trimethoxysilane, and stir for 10 minutes until the cross-linking agent is completely dissolved;

[0027] Add graphite thermal conductive particles D50 = 2 to 3 microns in batches, stir for 75 minutes, observe the uniformity, and perform vacuum defoaming for 45 minutes to obtain phase change graphite thermal conductive material sample 1.

Example Embodiment

[0028] Example 2

[0029] The components and contents of phase change thermal conductive materials are as follows:

[0030]

[0031]

[0032] Specific preparation method:

[0033] Add low-melting wax PE80, 2,2'-methylene-bis-(4-methyl, 6-tert-butylphenol), coupling agent isopropyl three oil in the planetary power mixer according to the formula ratio Acid acyloxy titanate, raise the temperature to 70 degrees Celsius, stir for 45 minutes to form a uniform paste;

[0034] Then add the cross-linking agent trimethoxysilane, and stir for 10 minutes until the cross-linking agent is completely dissolved;

[0035] Add graphite thermal conductive particles D50=3-5 microns in batches, stir for 75 minutes, observe that the mixture is uniform, and perform vacuum defoaming for 45 minutes to obtain phase change graphite thermal conductive material sample 2.

Example Embodiment

[0036] Example 3

[0037] The components and contents of phase change thermal conductive materials are as follows:

[0038]

[0039] Specific preparation method:

[0040] Add microcrystalline wax 70#, antioxidant 1076, coupling agent γ-methacryloxypropyltrimethoxysilane in the planetary power mixer according to the stated formula ratio, raise the temperature to 70 degrees Celsius, and stir for 45 Minutes into a uniform paste;

[0041] Then add the cross-linking agent titanium acetylacetonate, and stir for 10 minutes until the cross-linking agent is completely dissolved;

[0042] Add graphite thermal conductive particles D50 = 2 to 3 microns in batches, stir for 75 minutes, observe that the mixture is uniform, and perform vacuum defoaming for 45 minutes to obtain phase change graphite thermal conductive material sample 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a phase change graphite heat conduction material with high thermal conductivity. The phase change graphite heat conduction material with high thermal conductivity is composed of the following substances: 10-25% of base phase change resin, 0-5% of an antioxidant, 0-5% of a crosslinking agent, 1-5% of a coupling agent, and 40-80% of graphite heat conductive particles. The phase change graphite heat conduction material provided by the invention can be used for radiator interface heat dissipation and the like in the heat source component/LED assembly technology of semiconductor surface packaging, and greatly improves the heat dissipation effect and long-term reliability of heat source components and LED radiators. The product has the advantages of excellent surface wetting performance and fast and effective heat dissipation effect, good electrical performance, low cost, and especially excellent long term use effect. The preparation method of the product is simple, can be applied to mechanical process and manual use, etc., can meet the increasingly high heat dissipation requirements of high-end electronic products, like PC, game machines and high power LED.

Description

technical field [0001] The invention relates to a phase-change graphite heat-conducting material with high thermal conductivity and a preparation method thereof, and is especially suitable for interface heat dissipation of heat source components in semiconductor surface packaging or radiators in an LED assembly process. Background technique [0002] With the vigorous development of electronic technology in the 21st century, the heat density of various electronic components is getting higher and higher, and the heat dissipation problem has become a crucial consideration in the design of electronic products. [0003] Compared with the heat-conducting silicone grease commonly found in the market, the present invention has low initial thermal resistance and excellent heat transfer performance; because it is a phase-change material, the product changes form as the temperature changes, from solid to liquid, and can provide a certain amount of latent heat ;The product returns to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L91/06C08L23/06C08K13/02C08K3/04C09K5/06
CPCC08K13/02C08K3/04C08K2201/003C09K5/066C08L91/06C08L23/06
Inventor 邓志军万炜涛陈田安
Owner SHENZHEN DARBOND INTERFACE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap