A self-leveling mortar and wear-resistant technology, applied in the field of building materials, can solve the problems of resource and environmental hazards, slow strength development, fast drying shrinkage, etc., and achieve the effects of improving early strength, fast strength development, and low shrinkage rate.
Inactive Publication Date: 2016-03-30
JIANGXI BEIRONG CIRCULAR MATERIALS CO LTD
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In recent years, due to the massive mining of machine-made sand and river sand, it has caused serious harm to resources and the environment. At the same time, some
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] A high-strength wear-resistant self-leveling mortar, which is uniformly mixed with the following components by weight:
[0018] Cement: 36 parts
[0019] Slag: 4.0 parts
[0020] River sand: 15.1 parts
[0021] Pyrite tailings: 28.6 parts
[0022] Water: 16.7 parts
[0023] Redispersible latex powder: 2 parts
[0024] Water reducing agent: 0.2 parts
[0025] Shrinkage reducer: 1.5 parts
[0026] Water retaining agent: 0.06 part
[0027] Antifoaming agent: 0.15 parts.
Embodiment 2
[0029] A high-strength wear-resistant self-leveling mortar, which is uniformly mixed with the following components by weight:
[0030] Cement: 31 parts
[0031] Slag: 8.0 parts
[0032] River sand: 11.1 parts
[0033] Pyrite tailings: 32.9 parts
[0034] Water: 16.7 parts
[0035] Redispersible latex powder: 2 parts
[0036] Water reducing agent: 0.2 parts
[0037] Shrinkage reducer: 1.5 parts
[0038] Water retaining agent: 0.06 part
[0039] Antifoaming agent: 0.15 parts.
Embodiment 3
[0041] A high-strength wear-resistant self-leveling mortar, which is uniformly mixed with the following components by weight:
[0042] Cement: 27.8 parts
[0043] Slag: 11.9 parts
[0044] River sand: 6.7 parts
[0045] Pyrite tailings: 37.3 parts
[0046] Water: 16.7 parts
[0047] Redispersible latex powder: 2 parts
[0048] Water reducing agent: 0.2 parts
[0049] Shrinkage reducer: 1.5 parts
[0050] Water retaining agent: 0.06 part
[0051] Antifoaming agent: 0.15 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
Environment-friendly high-strength wear-resistant self-leveling mortar belongs to the field of building materials. The mortar is prepared from cement, a mineral admixture, pyrite tailings, natural sand, an additive and water; the mass ratio of the cement to the mineral admixture is (0.5-1) to (0-0.5); the mass ratio of the natural sand to pyrite tailings is 1 to (0.9-1.6). In the invention, the cement is used as a cementitious material; a secondary pozzolanic reaction is performed by using a cement hydrated product, high-activity mineral slags and pyrite tailing fine powder to produce more cementitious substances, thereby enhancing the early strength of the self-leveling mortar. The self-leveling mortar has an excellent vibration-free performance, and the surface after construction is flat and smooth and the mortar can be used as disposable clear water decorative floor, and is fast in strength development, low in shrinkage and high in wear resistance.
Description
technical field [0001] The invention belongs to building materials, in particular to a cement-based self-leveling mortar. Background technique [0002] Self-leveling mortar is a dry-mixed powdery material composed of a variety of active ingredients. It can be used after mixing with water on site. After a little spreading with a scraper, a high-level base surface can be obtained. The hardening speed is fast, and it can be walked on in 24 hours. Or carry out follow-up finishing layer engineering (such as laying wood boards, gold steel plates, etc.), the construction is quick and easy. The main material of self-leveling mortar is composed of cementitious material, fine aggregate, redispersible latex powder, water reducer, shrinkage reducer, water retaining agent, water, etc. in a certain proportion. In recent years, due to the massive mining of machine-made sand and river sand, it has caused serious harm to resources and the environment. At the same time, some cement-based sel...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more