A kind of composite sound insulation material and preparation method thereof

A sound insulation material and sound volume technology, applied in the field of sound insulation materials, can solve the problems of limited application range, high cost, bulky and thick

Active Publication Date: 2018-07-13
KUNMING IRON & STEEL HLDG CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to effectively block noise, most traditional sound insulation materials are solved by increasing surface density and thickness, which are very heavy and thick, complicated processing procedures and high cost, which limit their application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite sound insulation material and preparation method thereof
  • A kind of composite sound insulation material and preparation method thereof
  • A kind of composite sound insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] Such as figure 1 Shown: the preparation method of described composite sound insulation material comprises the steps:

[0039] (1) Measuring and preparing materials: Weigh each component according to the mass fraction, stir the recycled steel slag powder and coupling agent in a high-mixer for 5-10 minutes, and control the stirring temperature at 90-110°C to complete the steel slag powder Surface activation treatment;

[0040] (2) Sequential feeding and high-speed dispersion: first add recycled polyethylene, linear low-density polyethylene and polymer compatibilizer to the mixed materials in step (1), stir at high speed for 3-5 minutes, and control the stirring temperature at 70- 80°C; then add diluent and antioxidant, stir at high speed for 3-5 minutes, and control the stirring temperature at 70-90°C;

[0041] (3) Mixing and plasticizing: put the mixed material in step (2) into the mixer and knead for 15-20 minutes, and the mixing temperature is ≤160°C for further plas...

Embodiment 1

[0052] The components are prepared according to Table 1.

[0053]Table 1 Mass fraction of each component

[0054]

[0055] The preparation steps are as follows:

[0056] (1) Stir 75% steel slag powder and 1% silane coupling agent in a high mixer for 10 min, and control the stirring temperature at 110°C to complete the activation treatment on the surface of steel slag powder.

[0057] (2) Put 15% recycled polyethylene, 5% linear low density polyethylene and 2.5% maleic anhydride grafted polyethylene into the mixed material in step (1) and stir at high speed for 5 minutes, and the stirring temperature is controlled at 80°C; Then add 1% chlorinated paraffin 42, 0.3% antioxidant 1010 and 0.2% antioxidant 168, stir at high speed for 5 min, and control the stirring temperature at 90 °C.

[0058] (3) Put the mixed material in step (2) into the internal mixer and knead for 20 minutes. The temperature of each section of the internal mixer is ≤160°C for further plasticization.

[...

Embodiment 2

[0064] The components are prepared according to Table 3.

[0065] Table 3 Mass fraction of each component

[0066]

[0067] The preparation steps are as follows:

[0068] (1) Stir 65% steel slag powder and 1.2% titanate coupling agent in a high mixer for 8 minutes, and control the stirring temperature at 100°C to complete the activation treatment on the surface of steel slag powder.

[0069] (2) Put 18% recycled polyethylene, 8% linear low density polyethylene and 5% maleic anhydride grafted ethylene-vinyl acetate copolymer into the mixed material in step (1) and stir for 4 minutes at high speed, and the stirring temperature is controlled at 75°C; then add 2% chlorinated paraffin 52, 0.5% antioxidant 1010 and 0.3% antioxidant 168, stir at high speed for 4 min, and control the stirring temperature at 80°C.

[0070] (3) Put the mixed material in step (2) into the internal mixer and knead for 18 minutes. The temperature of each section of the internal mixer is ≤160°C for fur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite sound-insulation material and a preparation method thereof. The composite sound-insulation material is composed of the following components in percentage by mass: 65-75% of reclaimed steel slag powder, 10-20% of reclaimed polyethylene, 5-10% of linear low-density polyethylene, 2.5-5% of high-polymer compatilizer, 1-2% of diluter, 1-2% of coupling agent and 0.5-1% of antioxidant. The preparation method comprises the following steps: metering and preparing materials, sequentially adding the materials, dispersing at high speed, banburying, plastifying, extruding, calendering and the like. The steel scrap slag and waste plastic are recycled, thereby implementing reutilization of the waste resources. The composite sound-insulation material has the advantages of low cost, high constructability and the like, is easy for secondary processing and applicable to sound insulation treatment of irregular objects.

Description

technical field [0001] The invention belongs to the technical field of sound insulation materials, and in particular relates to a vinyl sound insulation composite material prepared by filling with recycled steel slag powder and a preparation method thereof. Background technique [0002] With the development and utilization of the natural environment by people, there are more or less shortages of various resources on the earth. The traditional way of relying on resource consumption to achieve economic development will become difficult in the future. At this time, turning waste into resources again to reduce the amount of final disposal, that is, what we usually call waste recycling and comprehensive utilization of waste, can also be called "recycling", and has become one of the hotspots of people's research. one. [0003] Steel slag is a kind of industrial waste slag produced during steelmaking, and its quantity is generally 10% to 20% of crude steel output, and the amount ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/08C08L51/06C08K11/00
CPCC08K2201/003C08L23/06C08L23/0815C08L2201/02C08L2201/08C08L2205/035C08L2207/20C08L51/06C08K11/005
Inventor 刘瑞铭严杨刘畅赵华玲
Owner KUNMING IRON & STEEL HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com