Automobile interior trim material capable of removing formaldehyde

A technology for automotive interior decoration and formaldehyde, which is applied in biochemical fiber treatment, textiles and papermaking, fiber treatment, etc., can solve the problems of only sporadic reports in the application, and achieve the advantages of improving acid and alkali resistance, simple operation, improving heat resistance and toughening Effect

Inactive Publication Date: 2016-04-20
芜湖跃飞新型吸音材料股份有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most PLA modified materials are mainly used in food packaging, medical equipment and other fields, but there are only sporadic reports on the application of automotive interior parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] An automotive interior material capable of purifying formaldehyde, made of the following raw materials in parts by weight (kg): bamboo fiber 30, antimony trioxide 2, shell powder 5, water-based polyurethane 10, silane coupling agent kh5700.2, poly Ethylene wax 1, polyvinyl alcohol 10, polylactic acid 100, dimethylacetamide 60, dimethyl sulfoxide 30, carbonized green dill 9.6, microcrystalline stone powder 9.5, polybutylene succinate 6, acrylic emulsion 10, Appropriate amount of deionized water;

[0014] Described a kind of car trim material that can purify formaldehyde is prepared by the following specific steps:

[0015] (1) Dry the bamboo fiber at 105°C for 2 hours and then open it. Add antimony trioxide and shell powder to the water-based polyurethane emulsion (solid content is 20%) and stir evenly, then impregnate the bamboo fiber into the water-based polyurethane In the emulsion, heat to 100°C under 2Pa and keep it at a constant temperature until the water evapora...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an automobile interior trim material capable of removing formaldehyde. The automobile interior trim material is prepared from, by weight, 30-35 parts of bamboo fiber, 2-3 parts of antimonous oxide, 5-7 parts of shell powder, 10-12 parts of waterborne polyurethane, 0.2-0.4 part of a silane coupling agent kh570, 1-2 parts of polyethylene wax, 10-13 parts of polyvinyl alcohol, 100-105 parts of polylactic acid, 60-68 parts of dimethylacetamide, 30-35 parts of dimethyl sulfoxide, 9.6-10.7 parts of carbonized scindapsus aureus, 9.5-10.5 parts of microlite powder, 6-7 parts of poly(butylene succinate), 10-12 parts of acrylic emulsion and an appropriate amount of deionized water. According to the automobile interior trim material, operation is easy, the raw material sources are wide, the biodegradability is good, toxic substances such as formaldehyde in an automobile can be removed, air can be purified, and a healthy and comfortable environment can be built.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an automobile interior material capable of purifying formaldehyde. Background technique [0002] Polylactic acid (PLA) is a polymer obtained by polymerization of lactic acid as the main raw material. Its production process is non-polluting and biodegradable, so it is an ideal green polymer material. In recent years, the application of PLA in the fields of automotive interior, textile, packaging and medicine has been greatly developed. Because of its non-toxic, good biocompatibility, biodegradability and final degradation products are CO2 and H2O, and its performance can be adjusted in a wide range by methods such as copolymerization, blending, molecular modification, and compounding, It has become one of the most valued materials at present. PLA has good strength and rigidity, but poor flexibility, impact performance and heat resistance. If it is used in occasions re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L97/02C08L75/04C08L29/04C08L67/02C08K13/06C08K9/06C08K9/10C08K3/04C08K3/34D06M15/564D06M11/47D06M11/76D06M101/06
CPCC08L67/04C08L2201/02C08L2201/06C08L2201/08C08L2205/02C08L2205/035C08L2205/16D06M11/47D06M11/76D06M15/564D06M16/00D06M2101/06D06M2200/30C08L97/02C08L75/04C08L29/04C08L67/02C08K13/06C08K9/10C08K9/06C08K3/04C08K2003/265
Inventor 王黎明章云
Owner 芜湖跃飞新型吸音材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap