Industrial super-convenient superhydrophobic finish-coat paint and preparation method thereof
A super-hydrophobic, water-covering technology, applied in the coating and other directions, can solve the problems of harsh reaction, lengthy time and complicated process of super-hydrophobic topcoat, and achieve the effect of being conducive to industrialization, simple operation and convenient process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] The preparation method of the industrialized super convenient super hydrophobic finish paint includes the following steps:
[0034] ①Preparation of transparent precursor solution: Add ethanol, water and hexadecyltrimethoxysilane to ethyl orthosilicate while stirring at 250rpm, and stir for 8h in a 70℃ water bath at 350rpm to obtain a transparent precursor Solution ready for use;
[0035] ②Preparation of particle compounding liquid: mixing nano colloidal silicon aqueous dispersion R301 and nano colloidal silicon aqueous dispersion R1050 in a weight ratio of 7:3, and dispersing at 350rpm for 30min to obtain particle compounding liquid;
[0036] ③ Mixing of transparent precursor liquid and particle compounding liquid: add transparent precursor solution to particle compounding liquid and disperse for 30min, wherein the weight ratio of transparent precursor liquid to particle compounding liquid is 4:1, that is, the industrialized preparation Super convenient and super hydrophobic ...
Example Embodiment
[0037] Example 2
[0038] An industrialized super-convenient and super-hydrophobic topcoat, which comprises: it is formulated with the following parts by weight,
[0039]
[0040] The preparation method of the industrialized super convenient super hydrophobic finish paint includes the following steps:
[0041] ① Preparation of transparent precursor solution: add ethanol, water and hexadecyltrimethoxysilane to ethyl orthosilicate while stirring at 200 rpm, and stir at medium speed at 400 rpm for 8 hours in a 70℃ water bath. The transparent precursor solution is ready for use;
[0042] ②Preparation of particle compounding liquid: mixing nano colloidal silicon aqueous dispersion R301 and nano colloidal silicon aqueous dispersion R1050 in a weight ratio of 7:3, and dispersing at 300 rpm for 30 min to obtain particle compounding liquid;
[0043] ③Mixing of transparent precursor liquid and particle compounding liquid: Add the transparent precursor solution to the particle compounding liquid ...
Example Embodiment
[0044] Example 3
[0045] A super-convenient and super-hydrophobic finish paint that can be industrialized, which includes:
[0046]
[0047] The preparation method of the industrialized super convenient super hydrophobic finish paint includes the following steps:
[0048] ① Preparation of transparent precursor solution: Add ethanol, water and hexadecyltrimethoxysilane to ethyl orthosilicate while stirring at a rotation speed of 300 rpm, and stir for 8 hours in a 70 ℃ water bath at 300 rpm to obtain a transparent precursor. Solution ready for use;
[0049] ② Preparation of particle compounding liquid: mixing nano colloidal silicon aqueous dispersion R301 and nano colloidal silicon aqueous dispersion R1050 in a weight ratio of 1:1, and dispersing at 400 rpm for 30 minutes to obtain particle compounding liquid;
[0050] ③ Mixing of transparent precursor liquid and particle compounding liquid: add transparent precursor solution to particle compounding liquid and disperse for 30min, wherei...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap