A kind of peelable nail polish and its synthesis method
A synthetic method and technology of nail polish, applied in manicure, pharmaceutical formula, pedicure, etc., can solve the problems of inconvenient production and use of nail polish, not as durable as oily nail polish, slow drying, etc., and achieve easy control , high toughness, easy peeling effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0037] A peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:
[0038]
[0039] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:
[0040]
[0041] The UV curable resin A is prepared according to the following steps: 20 parts of methylphenyl hydrogen-containing silicone oil and 10 parts of propoxylated glycerin triacrylate are added to a 500ml three-necked flask, and then 0.005 of a polymerization inhibitor is added. Protect the gas, stir and heat, raise the temperature to 60°C, add 0.03 part of catalyst, keep the temperature under stirring for 3 hours, stop heating, wait until the temperature of the flask drops to room temperature, and obtain UV curable resin A.
[0042] The leveling agent is Tego Glide 410;
[0043] Described wetting agent is NP-100 of U.S. Dow Company;
[0044] The defoamer is a mixture of German BYK-035 and BYK-037 in a mas...
Embodiment 2
[0054] A peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:
[0055]
[0056]
[0057] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:
[0058]
[0059] The UV curable resin A is prepared according to the following steps: 60 parts of methylphenyl hydrogen-containing silicone oil and 20 parts of propoxylated glycerin triacrylate are added to a 500ml three-necked flask, and then 0.01 part of a polymerization inhibitor is added. Protect the gas, stir and heat, raise the temperature to 80°C, add 0.05 part of catalyst, keep the temperature under stirring for 5 hours, stop heating, wait until the temperature of the flask drops to room temperature, and obtain UV curable resin A.
[0060] The leveling agent is a mixture of German BYK-345 and BYK-346 in a mass ratio of 1:1;
[0061] The wetting agent is German BYK 333;
[0062] The defoamer is a ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| peel strength | aaaaa | aaaaa |
| peel strength | aaaaa | aaaaa |
| peel strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More