A kind of glass fiber reinforced PBT composition and its preparation method and application

A technology of composition and PBT resin, applied in the field of PBT composition, to achieve the effect of improving the filling rate of profiles

Active Publication Date: 2018-05-01
KINGFA SCI & TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] So far, the content of tetrahydrofuran has no effect on the profile filling rate of the glass fiber reinforced PBT composition and the PVC profile during the co-extrusion process, the adhesion between the glass fiber reinforced PBT composition and PVC, and the degree of warpage of the profile. to report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-9 and comparative example 1-9

[0052]Preparation of glass fiber reinforced PBT composition: Tetrahydrofuran and methyl siloxane are formulated into a tetrahydrofuran methyl siloxane solution with a mass fraction of 10ppm-900ppm; the tetrahydrofuran methyl siloxane solution is mixed with the PBT The resin and additives are mixed in a high-speed mixer for 1 minute to 2 minutes to obtain a premix, which is melted and extruded by a twin-screw extruder at 220°C-240°C, fed to the side of the glass fiber, cooled, and granulated to obtain Glass fiber reinforced PBT composition; the temperature of each screw barrel of the twin-screw extruder (from the feeding port to the head) is: 160°C, 220°C, 230°C, 240°C, 240°C, 220°C, and the screw speed is 300 rpm, feed rate 60kg / h.

[0053] Preparation of glass fiber reinforced PBT composition and PVC co-extruded profile: the glass fiber reinforced PBT composition and PVC prepared above are respectively passed through two single-screw extruders into the profile cavity, wherein...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass fiber reinforced PBT composition. The glass fiber reinforced PBT composition comprises, by weight, 40-70 parts of PBT resin and 30-60 parts of glass fibers; based on the total weight of the glass fiber reinforced PBT composition, the content of tetrahydrofuran is smaller than or equal to 450 ppm and greater than or equal to 25 ppm. According to the glass fiber reinforced PBT composition and the preparation method and application thereof, tetrahydrofuran is selected and added to the formula of the glass fiber reinforced PBT composition, wherein the content of tetrahydrofuran is smaller than or equal to 450ppm and greater than or equal to 25 ppm based on the total weight of the glass fiber reinforced PBT composition, so that when the glass fiber reinforced PBT composition and PVC are jointly used for extruding a profile, the filling rate of the profile can be obviously raised, cohesiveness of the glass fiber reinforced PBT composition and PVC can be obviously improved, and the warping degree of the profile can be obviously improved.

Description

technical field [0001] The invention relates to a PBT composition, in particular to a glass fiber reinforced PBT composition and its preparation method and application. Background technique [0002] Polybutylene terephthalate (PBT) is a semi-crystalline engineering plastic with good mechanical properties, electrical properties, heat resistance and chemical resistance, etc. It is widely used in automobiles, electronics, electrical appliances and other industries . However, PBT still has deficiencies, such as the low filling rate of PBT materials in the process of co-extruding profiles with PVC, the poor adhesion between PBT and PVC, and the degree of profile warping, which limits its application in the above industries. [0003] Under the premise of not affecting the mechanical and processing properties of PBT materials, the requirements for improving the profile filling rate, the adhesion between PBT materials and PVC, and the degree of warping of profiles during the co-ext...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08K7/14B29C47/92B29C48/92
CPCB29C48/92B29C2948/9258B29C2948/92704C08K7/14C08K2201/003C08L67/02
Inventor 陈锋朱文付学俊陈伟禹权丁超
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com