Improvement method of strip breaking process of multi-wire cutting machine

A multi-wire cutting machine and strip breaking technology, which is applied in the direction of manufacturing tools, work accessories, stone processing equipment, etc., can solve the problems of unqualified products at both ends, cutting precision knife lines, and unstable tension, so as to reduce auxiliary materials. Consumption, improve work efficiency, improve the effect of qualified rate

Active Publication Date: 2018-12-28
SINO MAGNETICS TECH
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the weight of the solid material plate and the whole glass used in the bonding process is about 40kg, and the manual handling is very laborious during the bonding process.
During the cooking process, the solid material plate and the glass are closely bonded, and it is not easy to boil if the time is short. If the time is long, the NaOH is corrosive and may cause damage to the product; during the cutting process of the multi-wire cutting machine, silicon carbide mortar is used continuously The steel wire is used to cut the product. During the continuous pouring process, due to the gap between the bonded block and the block, the mortar will be lost quickly after pouring into the product. The contact between the steel wire and the mortar is not sufficient, which will easily affect the cutting accuracy and cause the knife Moreover, in the process of pouring mortar, the front and rear ends of the whole sheet are not easy to be poured, and the front and rear ends are the inlet and outlet of steel wires, and the tension is unstable, so the probability of unqualified products at both ends is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Improvement method of strip breaking process of multi-wire cutting machine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] Specific embodiments of the present invention are described in detail below, but it should be understood that the protection scope of the present invention is not limited by the specific embodiments.

[0013] Unless expressly stated otherwise, throughout the specification and claims, the term "comprise" or variations thereof such as "includes" or "includes" and the like will be understood to include the stated elements or constituents, and not Other elements or other components are not excluded.

[0014] According to the specific embodiment of the present invention, a method for improving the strip breaking process of a multi-wire cutting machine includes the following steps: bonding the hollow material plate 1 with multiple pieces of glass in the bonding process, and the size of the multiple glass plates is the same And the form of multiple columns is presented on the hollow material plate 1, and there are first gaps with the same distance between each glass; multiple ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified method for the strip breaking technology of a multi-wire sawing machine. The modified method comprises the following steps: (1) splicing a hollow material plate with a plurality of glass plates together in a material splicing process, wherein the glass plates are the same in size, and arranged on the hollow material plate in a plurality of lines, a first gap is formed between every two adjacent glass plates, and all the first gaps are the same; (2) sticking a plurality of block materials on the glass plates, wherein a second gap is formed between every two adjacent block materials, and all the second gaps are the same; (3) splicing small glass pieces with the left and right sides of a whole-plate material obtained after the block materials are stuck on the glass plates, so as to plug gaps on the outer sides of the block materials, and splicing small glass pieces to the upper and lower ends of the whole-plate material and the outer sides the block materials. Therefore, due to the modified method, the product qualification rate can be improved, and quality problems such as tool marks can be solved.

Description

technical field [0001] The invention relates to an improved method for breaking a strip of a multi-wire cutting machine. Background technique [0002] At present, when using multi-wire cutting machines to process products, firstly, the entire glass cut to a certain size needs to be bonded to a clean and dry solid material board, and secondly, the block materials are glued together on the adhesive tooling, and then the The bonded glass material plate is placed on the positioning tool, and finally the bonded block material is bonded on the material plate according to the positioning. After the bonding is completed, use the Xiangyi forklift to send the bonded whole sheet to the equipment workbench for cutting. The processed product needs to be boiled for about 3 to 4 hours before being transported to the grinder. There is NaOH in the cooking pot to separate the material plate, glass, and processed strips into the next process. prepare for. [0003] At present, the weight of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28D5/04B28D7/04
CPCB28D5/045B28D7/04
Inventor 贾骞董俊安
Owner SINO MAGNETICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products