Heavy metal wastewater composite adsorbent and preparation method thereof
A composite adsorption and heavy metal technology, applied in water/sewage treatment, chemical instruments and methods, extraction water/sewage treatment, etc., can solve the problems of lack of types of airgel materials, limit the selection of sewage treatment materials, etc., and achieve high market application Prospect, easy adsorption, low cost effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1:
[0030] A composite adsorbent for heavy metal sewage, which is composed of the following raw materials in parts by weight: A composite adsorbent for sewage treatment, characterized in that it is composed of the following raw materials in parts by weight: zeolite 20; resorcinol 20; Triphenylphosphine 0.5; Furfural 8; Humic acid 1.0; Triethylene diamine 0.8; Methyl cellulose 3.0; Sodium dodecyl sulfonate 2.0; Graphene nanolayer / MnO2 composite 3.0; Chitosan -Graphene composite material 5.0. The preparation method is:
[0031] Step 1: The zeolite is calcined in a rotary kiln for 1 hour, the calcination temperature is 700℃, and the rotation speed of the rotary kiln is 5rpm; after calcination, it is naturally cooled to room temperature for later use;
[0032] Step 2: Grind and pulverize the calcined zeolite obtained in Step 1, and crush and sieve to 200 mesh;
[0033] Step 3: Add resorcinol, triphenylphosphine, furfural, humic acid and triethylenediamine to deionized wa...
Example Embodiment
[0040] Example 2:
[0041] A composite adsorbent for heavy metal sewage, which is composed of the following raw materials in parts by weight: zeolite 30; resorcinol 24; triphenylphosphine 0.9; furfural 12; humic acid 2.0; triethylenediamine 1.2; methyl fiber Sodium dodecyl sulfonate 4.0; Graphene nanolayer / MnO2 composite 6.0; Chitosan-graphene composite 10.0.
[0042] The preparation method is:
[0043] Step 1: The zeolite is calcined in a rotary kiln for 2 hours, the calcination temperature is 700℃, and the rotation speed of the rotary kiln is 10rpm; after calcination, it is naturally cooled to room temperature for later use;
[0044] Step 2: Grind and pulverize the calcined zeolite obtained in Step 1, and crush and sieve to 200 mesh;
[0045] Step 3: Add resorcinol, triphenylphosphine, furfural, humic acid and triethylenediamine to deionized water, and stir and mix at a heating temperature of 70°C, with a stirring speed of 900rpm and a stirring time of 10min;
[0046] Step 4: Add the ...
Example Embodiment
[0052] Example 3:
[0053] A composite adsorbent for heavy metal sewage, which is composed of the following raw materials in parts by weight: zeolite 25; resorcinol 22; triphenylphosphine 0.7; furfural 10; humic acid 1.5; triethylenediamine 1.0; methyl fiber Sodium dodecylsulfonate 3.0; Graphene nanolayer / MnO2 composite 5.0; Chitosan-graphene composite 8.0.
[0054] The preparation method is:
[0055] Step 1: The zeolite is calcined in a rotary kiln for 2 hours, the calcination temperature is 700°C, and the rotation speed of the rotary kiln is 8 rpm; after calcination, it is naturally cooled to room temperature for later use;
[0056] Step 2: Grind and pulverize the calcined zeolite obtained in Step 1, and crush and sieve to 200 mesh;
[0057] Step 3: Add resorcinol, triphenylphosphine, furfural, humic acid and triethylenediamine to deionized water, and stir and mix at a heating temperature of 70°C, with a stirring speed of 900rpm and a stirring time of 10min;
[0058] Step 4: Add the z...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap