HRB400 rebar and production method thereof

A production method and steel bar technology, applied in the field of metallurgy, can solve problems such as high cost, poor mechanical strength, and unstable performance

Inactive Publication Date: 2016-07-20
INNER MONGOLIA BAOTOU STEEL UNION
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing HRB400 steel bar has poor mechanical strength and unstable performance. In order to increase the strength of the steel bar, the existing technology also adopts rapid cool

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HRB400 rebar and production method thereof
  • HRB400 rebar and production method thereof
  • HRB400 rebar and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] The invention discloses a HRB400 steel bar and a production method thereof. Those skilled in the art can learn from the content of this article and appropriately improve the process parameters. In particular, it should be pointed out that all similar replacements and modifications are obvious to those skilled in the art, and they are all deemed to be included in the present invention. The method and application of the present invention have been described through the preferred embodiments. It is obvious that relevant persons can modify or appropriately change and combine the methods and applications described herein without departing from the content, spirit and scope of the present invention to achieve and Apply the technology of the present invention.

[0020] The present invention provides a HRB400 steel bar, which comprises: 0.19-0.25wt% C, 0.55-0.80wt% Si, 1.45-1.60wt% Mn, 0.20-0.30wt% Cr, and the balance iron.

[0021] In the HRB400 steel bar provided by the present i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of metallurgy, and particularly discloses an HRB400 rebar and a production method thereof. The HRB400 rebar is prepared from 0.19 wt%-0.25 wt% of C, 0.55 wt%-0.80 wt% of Si, 1.45 wt%-1.60 wt% of Mn, 0.20 wt%-0.30 wt% of Cr and the balance iron. The HRB400 rebar has the advantages of being excellent and stable in mechanical property and low in cost.

Description

technical field [0001] The invention relates to the field of metallurgy, in particular to a HRB400 steel bar and a production method thereof. Background technique [0002] HRB400 is the grade of threaded steel bar stipulated in "Steel for Reinforced Concrete" GB1499.2-2007. Due to the wide range of standard components and the differences in production equipment and process control of manufacturers, the HRB400 hot-rolled ribbed steel bars produced by various manufacturers are different. The composition is different, and the production process of each steel factory is also different. The existing HRB400 steel bar has poor mechanical strength and unstable performance. In order to increase the strength of the steel bar, the existing technology also adopts rapid cooling and fine-grain strengthening to improve the strength of the steel bar, or there are methods to improve the strength of the steel bar through microalloying. But the cost is higher. Contents of the invention [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/18C21D8/08
CPCC22C38/02C21D8/08C22C38/04C22C38/18
Inventor 吕刚戈春刚谭晓东
Owner INNER MONGOLIA BAOTOU STEEL UNION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap