High titanium slag self-compacting concrete production method

A technology of self-compacting concrete and preparation method, which is applied in the direction of clay preparation equipment, chemical instruments and methods, cement mixing equipment, etc., to achieve high utilization value, broaden the application field, and reduce costs

Active Publication Date: 2016-08-03
麻城市华林商砼建材有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing self-compacting concrete ingredients usually include pebbles, crushed stones, medium-fine sand and fly ash, etc. Usually, high-titanium slag sand and gravel are not used as concrete ingredients, and there is no mix ratio design method for high-titanium slag self-compacting concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be further described below in combination with specific embodiments.

[0016] The preparation method of high titanium slag self-compacting concrete comprises the following steps:

[0017] A. Prepare concrete ingredients. Concrete ingredients include high-titanium slag fine sand, high-titanium slag gravel, cement, fly ash, admixtures and water; the maximum particle size of high-titanium slag gravel is 16mm, and the apparent density is 2730kg / m 3 , bulk density is 1390kg / m 3 ;The fineness modulus of high titanium slag fine sand is 2.8, and the apparent density is 3130kg / m 3 , bulk density is 1770kg / m 3 ;

[0018] B. Determine the dosage of each ingredient;

[0019] The amount of high-titanium slag and crushed stone per cubic meter of concrete is determined according to the self-compacting performance level of the concrete. The specific method is as follows:

[0020] ;

[0021] Concrete water consumption per cubic meter according to the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high titanium slag self-compacting concrete production method, relates to the field of reuse of high titanium slag, and provides a production method of self-compacting concrete by adopting high titanium slag as an ingredient. The method comprises the following steps: 1, preparing the following concrete ingredients: high titanium slag fine sands, high titanium slag broken stones, cement, fly ash, an additive and water; and 2, determining the amounts of the ingredients, wherein the amount of the high titanium slag broken stones is determined according to the grade of the self compacting performance of concrete; the amount of water is determined according to a formula of V<w> = V<W1> + V<W2> - V<W3>; the amount of cement and fly ash is determined according to a ratio of the mass of water to the total mass of cement and fly ash and the admixture of the fly ash of 25-35%; the amount of the additive is determined according to test of the compatibility between the additive and cement; and the amount of the high titanium slag fine sands is obtained through determining the unit weight of concrete according to common high titanium slag concrete preparation experiences and subtracting the weight of the high titanium broken stones, cement, fly ash, the additive and water from the total unit weight. The method can be applied to concrete production.

Description

technical field [0001] The invention relates to the field of high titanium slag reuse, in particular to a method for preparing self-compacting concrete by using high titanium slag. Background technique [0002] At present, there is no unified method for the mix ratio design of self-compacting concrete at home and abroad. The mix ratio design methods proposed by domestic and foreign scholars mainly include: fixed sand and gravel volume method, full calculation method, improved full calculation method, parameter design method, Aggregate specific surface area method, simple mix ratio design method, etc. The calculation methods of self-compacting concrete mix ratio are not the same, each has its own characteristics and targets, and the design of self-compacting concrete mix ratio cannot be templated. With the development of extensive use of new industrial solid waste materials and high-efficiency water reducers, the calculation method of the mix ratio needs to be improved. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00B28C5/00
CPCB28C5/003C04B28/00C04B18/141C04B18/08
Inventor 陈伟李林泽王伟钟菘
Owner 麻城市华林商砼建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products