Foaming TPU color insole or shoe sole and production method thereof

A manufacturing method and technology for insoles, which are applied in the field of foaming TPU color soles and insoles and their manufacturing, can solve problems such as environmental pollution, environmental pollution, and human hazards, and achieve the effect of good elasticity

Inactive Publication Date: 2016-08-03
广东康诚新材料科技股份有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the materials of soles or insoles on the market mainly include the following types: TPR, RB, EVA, PU, ​​TPU, etc. The soles or insoles made of the above materials are relatively heavy except for EVA and PU materials, which are relatively light. Moreover, materials such as TPR, RB, and EVA are not environmentally friendly, and currently the soles or insoles need to be painted and painted in color to make them colorful, which will first pollute the environment, and more importantly, bring harm to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention relates to a kind of foaming TPU color insole or sole, comprising:

[0029] Liquid PU foaming material: 40 parts by weight;

[0030] Solid colored TPU foam particles: 60 parts by weight;

[0031] Among them, liquid PU foaming materials include:

[0032] Material A: 100 parts by weight;

[0033] Material B: 70 parts by weight;

[0034] Among them, material A includes: polyester polyol: 18KG, solid ammonia front-stage catalyst: 350G, isopropanol ammonia rear-stage catalyst: 80G, water: 180G, silicone oil: 360G, pigment: 300G;

[0035] Material B is isocyanate.

[0036] A kind of manufacture method of foaming TPU color insole, comprises the steps:

[0037] Step 1: Preheating of raw materials: put polyester polyol and isocyanate in an oven at 70°C and bake for 4 hours;

[0038] Step 2: Prepare materials: weigh solid ammonia, isopropanol ammonia, water, foam stabilizer, and pigments and put them into polyester polyol, mix and stir and pour into PU...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of shoes and particularly relates to a foaming TPU color insole or shoe sole which comprises 40 weight parts of liquid PU foaming material and 60 weight parts of solid color TPU foaming particles, wherein the liquid PU foaming material comprises 100 weight parts of material A and 70 weight parts of material B; the material A comprises 18KG of polyester polyol, 350G of ammonia fixing pre-catalyst, 80G of isopropyl ammonia post-catalyst, 180G of water, 360G of silicone oil and 300G of pigment; and the material B is isocyanate.

Description

technical field [0001] The invention relates to the field of shoes, in particular to a foamed TPU colored sole and insole with lightness, high elasticity, a boosting effect during exercise, dazzling and colorful, environmentally friendly, and concave-convex texture, and a manufacturing method thereof. Background technique [0002] At present, the materials of soles or insoles on the market mainly include the following types: TPR, RB, EVA, PU, ​​TPU, etc. The soles or insoles made of the above materials are relatively heavy except for EVA and PU materials, which are relatively light. Moreover, materials such as TPR, RB, and EVA are not environmentally friendly, and currently the soles or insoles need to be painted or painted in color to make them colorful, which firstly causes pollution to the environment, and more importantly, brings harm to the human body. Contents of the invention [0003] In order to solve the above problems, the present invention provides a foamed TPU ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L75/06C08G18/42
CPCC08L75/04C08G18/42C08L2203/14C08L2205/02C08L75/06
Inventor 田心花
Owner 广东康诚新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products