tialcrn&mos2/ti/al/cr multi-layered lubricating coating tool and its preparation process

A lubricating coating and cutting tool technology, applied in metal material coating process, coating, vacuum evaporation coating and other directions, to achieve the effect of reducing friction, high hardness and improving cutting performance

Active Publication Date: 2018-09-28
安徽锦鹏纺织有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the invention is to improve the overall performance of the existing coating tool, combining the advantages of multi-component hard coating and lubricating coating, to provide a TiAlCrN&MoS 2 / Ti / Al / Cr multi-layer lubricating coating tool and its preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • tialcrn&mos2/ti/al/cr multi-layered lubricating coating tool and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of TiAlCrN&MoS 2 / Ti / Al / Cr multi-layer lubricating coating tool, the tool is an ordinary milling insert, and its base material is: cemented carbide YT15. The deposition method is a composite coating method of unbalanced magnetron sputtering + arc plating + intermediate frequency magnetron sputtering. Two unbalanced magnetron sputtering targets are used for deposition: 1 Ti target, 1 Al target, and 1 arc Cr target, 2 MoS 2 Intermediate frequency sputtering target. First, unbalanced magnetron sputtering is used to deposit Ti transition layer, followed by unbalanced magnetron sputtering + arc ion plating composite deposition of Ti / Al / Cr transition layer, and then alternate deposition of TiAlCrN and MoS 2 / Ti / Al / Cr multi-layer multi-layer coating, the final surface is MoS 2 / Ti / Al / Cr composite lubricating coating. Its preparation process is:

[0028] (1) Pre-treatment: Polish the surface of the tool base to remove surface oil, rust and other impurities, then put ...

Embodiment 2

[0039] A kind of TiAlCrN&MoS 2 / Ti / Al / Cr multi-layer lubricating coating tool, the tool is an ordinary twist drill, and the tool base material is: high-speed steel W18Cr4V. The deposition method is a composite coating method of unbalanced magnetron sputtering + arc plating + intermediate frequency magnetron sputtering. Two unbalanced magnetron sputtering targets are used for deposition: 1 Ti target, 1 Al target, and 1 arc Cr target, 2 MoS 2 Intermediate frequency sputtering target. First, unbalanced magnetron sputtering is used to deposit Ti transition layer, followed by unbalanced magnetron sputtering + arc ion plating composite deposition of Ti / Al / Cr transition layer, and then alternate deposition of TiAlCrN and MoS 2 / Ti / Al / Cr multi-layer multi-layer coating, the final surface is MoS 2 / Ti / Al / Cr composite lubricating coating. Its preparation process is:

[0040] (1) Pre-treatment: Polish the surface of the tool base to remove surface oil, rust and other impurities, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of mechanically manufactured metal cutting tools, and particularly relates to a TiAlCrN&MoS2 / Ti / Al / Cr multi-element laminated lubricating coating tool and a preparation process thereof. A tool base body comprises high-speed steel, hard alloy, ceramics, diamond or cubic boron nitride. A MoS2 / Ti / Al / Cr lubricating coating is arranged on the surface of the tool, and a laminated structure coating with a Ti transition layer, a Ti / Al / Cr transition layer, a TiAlCrN hard coating and a MoS2 / Ti / Al / Cr lubricating coating alternating is sequentially arranged between the base body and the surface of the coating. According to the method, the advantages of a multi-element hard alloy, the lubricating coating, the laminated structure and three coating preparation methods are synthesized, high hardness is achieved, a lubricating function and a low friction coefficient are achieved, and the performance of the coating tool is remarkably improved.

Description

technical field [0001] The invention belongs to the field of mechanical manufacturing metal cutting tools, in particular to a TiAlCrN&MoS 2 / Ti / Al / Cr multi-layer lubricating coating tool and its preparation process. Background technique [0002] According to the nature of the coating material, coated tools can be divided into two categories, namely: "hard" coated tools and "lubricated" coated tools. The main advantages of "high hardness" coating tools are high hardness and good wear resistance. Typical "high hardness" coating materials include TiN, TiCN, TiAlN and diamond-like carbon. The goal pursued by "lubricating" coating tools is low friction coefficient. Typical "lubricating" coating materials are solid lubricating materials with low friction coefficients (such as: MoS 2 、WS 2 、TaS 2 and other sulfides). The current development trend of tool coatings is: coating components tend to be diversified and compounded. Composite coatings can combine the advantages of sin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/35C23C14/16C23C14/18C23C14/06C23C14/32C23C14/02
CPCC23C14/021C23C14/022C23C14/0623C23C14/0641C23C14/16C23C14/165C23C14/18C23C14/185C23C14/325C23C14/35
Inventor 宋文龙邓建新王首军郭宗新周珂李小冬
Owner 安徽锦鹏纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap