Method for producing fluorescent fabric for medical first-aid kit
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and fabric technology, applied in the field of medical rescue, can solve the problems such as the unsustainable fluorescent effect and the bad smell of the fabric, and achieve the effects of lastingly maintaining the fluorescent characteristics, improving the lasting luminosity, improving the waterproof performance and the wear-resistant life.
Inactive Publication Date: 2016-08-31
ANHUI TIANEN TRAVEL GOODS TECH CO LTD
View PDF2 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Existing fluorescent fabrics used for medical first aid kits mainly have defects such as the unsustainable fluorescent effect and the bad smell caused by soaking in fluorescent agents.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] A method for manufacturing fluorescent fabrics for medical first aid kits, the steps are as follows:
[0018] 1) Soak the blended fiber in fluorescent agent at 40°C for 3 hours, then dry after soaking.
[0019] The fluorescent agent consists of dioctyl phthalate, petroleum ether, film-forming aids, Al 2 o 3 , organic phosphine silane coupling agent and photo-induced energy storage luminous powder mixed. At room temperature, first add 3 parts of dioctyl phthalate and 12 parts of petroleum ether into the container, after stirring evenly, add 1 part of film-forming aid and 5 parts of Al 2 o 3 , then raise the temperature to 45°C, add 1 part of organophosphine silane coupling agent into the container, then slowly add 50 parts of photoluminescent energy storage luminous powder in 10 batches, and finally stir for 3 hours.
[0020] The structural formula of organophosphine silane coupling agent is:
[0021]
[0022] 2), process blended fiber into blended fabric.
[00...
Embodiment 2
[0026] A method for manufacturing fluorescent fabrics for medical first aid kits, the steps are as follows:
[0027] 1) Soak the blended fiber in the fluorescent agent, the soaking temperature is 50°C, the soaking time is 2h, and then dried after soaking.
[0028] The fluorescent agent consists of dioctyl phthalate, petroleum ether, film-forming aids, Al 2 o 3 , organic phosphine silane coupling agent and photo-induced energy storage luminous powder mixed. At room temperature, first add 12 parts of dioctyl phthalate and 1 part of petroleum ether into the container, after stirring evenly, add 5 parts of film-forming aid and 1 part of Al 2 o 3 , then raise the temperature to 35°C, add 5 parts of organophosphine silane coupling agent into the container, then slowly add 30 parts of photoluminescent energy storage luminous powder in 10 batches, and finally stir for 3 hours.
[0029] The structural formula of organophosphine silane coupling agent is:
[0030]
[0031] 2), pr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of medical aids, and specifically to a method for producing a fluorescent fabric for a medical first-aid kit. Blended fibers are placed into a fluorescent agent for soaking and then dried, in which the fluorescent agent is made from such raw materials as dioctyl phthalate and an organic phosphonic coupling agent; the blended fibers are processed into a blended fabric; the blended fabric is coated with a layer of waterproof adhesive; afterwards, the blended fabric is plasticized. The method for producing a fluorescent fabric for a medical first-aid kit provided by the present invention allows the fluorescent agent to be absorbed by the blended fibers to an utmost extent such that the produced fluorescent fabric is able to keep the fluorescent properties persistently. Particularly, the fluorescent agent is added with the component organic phosphonic coupling agent component that is capable of remarkably improving the persistent luminescence of a photo-induced energy-storage luminous powder in the fluorescent agent as compared to a traditional silicone coupling agent. The waterproofness and friction durability of the fabric can be remarkably improved by means of application of the waterproof adhesive and plasticization to the blended fabric.
Description
technical field [0001] The invention relates to the technical field of medical rescue, in particular to a method for manufacturing fluorescent fabrics used in medical first aid kits. Background technique [0002] The application of fluorescent fabrics to luggage products is an emerging technology that has gradually developed in recent years, especially for medical first aid kits, which can give pedestrians or vehicles warnings to ensure the personal safety of emergency personnel. The existing fluorescent fabrics used for medical first-aid kits mainly have defects such as that the fluorescent effect cannot be sustained, and the fabrics are soaked in fluorescent agents to cause a certain bad smell. Contents of the invention [0003] The object of the present invention is to provide a kind of manufacture method that is used for the fluorescent fabric of medical emergency kit, in order to realize above-mentioned object, the present invention adopts following technical scheme: ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more