Transparent back glue used for double-face color development hot stamping foil

A color-developing electrochemical aluminum and hot stamping foil technology, applied in the direction of adhesives, adhesive types, adhesive additives, etc., can solve the deviation of the transparency of the adhesive material, the reverse color layer can not normally develop color, double-sided color development electrochemistry Aluminum hot stamping foil manufacturing and popularization difficulties and other problems, to achieve the effect of high transparency and good slitting

Inactive Publication Date: 2016-10-05
ZHEJIANG HENGFENG PACKING
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of the production process and technology of the conventional anodized hot stamping foil adhesive, the transparency of the adhesive material is relatively biased. During the use process, fumed silica powder needs to be added, so that the color layer on the reverse side cannot develop color normally, and the double-sided color development is electrochemical. The manufacture and promotion of aluminum hot stamping foil has brought great difficulties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A transparent adhesive for double-sided color-developing electrochemical aluminum hot stamping foil and a preparation method thereof, comprising the following method steps:

[0018] 1) Put 120 parts of deionized water into the container first, and keep the temperature of the deionized water at 15°C to 25°C under low-speed stirring;

[0019] 2), under low-speed stirring, mix 13 parts of water-based polyurethane resin, 6 parts of water-soluble rosin modified phenolic resin, 5 parts of water-based amino resin, 0.5 part of defoamer, 1.2 parts of film-forming aid, 1.6 parts of wetting agent Put them into the container according to the proportion in turn, first stir at low speed for 20-30 minutes, then stir at high speed for 5-10 minutes;

[0020] 3) Stop stirring, control the temperature in the container at 20-25°C, and keep it for 30 minutes;

[0021] 4), the final strainer is filtered and poured into standby.

Embodiment 2

[0023] A transparent adhesive for double-sided color-developing electrochemical aluminum hot stamping foil and a preparation method thereof, comprising the following method steps:

[0024] 1) Put 100 parts of deionized water into the container first, and keep the temperature of the deionized water at 15°C to 25°C under low-speed stirring;

[0025] 2) Under low-speed stirring, mix 6 parts of water-based polyurethane resin, 10 parts of water-soluble rosin-modified phenolic resin, 7 parts of water-based amino resin, 0.3 part of defoamer, 0.7 part of film-forming aid, and 1 part of wetting agent Put them into the container according to the proportion in turn, first stir at low speed for 20-30 minutes, then stir at high speed for 5-10 minutes;

[0026] 3) Stop stirring, control the temperature in the container at 20-25°C, and keep it for 30 minutes;

[0027] 4), the final strainer is filtered and poured into standby.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to transparent back glue used for a double-face color development hot stamping foil and solves a problem of influence on color development on the last one coating due to poor transparency of a coated back glue layer in the prior art. The transparent back glue includes, by weight, 5-18 parts of aqueous polyurethane resin, 5-10 parts of aqueous rosin-modified phenolic resin, 0-10 parts of aqueous amino resin, 0.1-0.5 parts of a defoamer, 0.5-2 parts of a film-forming aid, 0-2 parts of a wetting agent, and 60-120 parts of deionized water. The transparent back glue is free of addition of fumed silica powder into the glue material during usage, and has high transparency and good cutting property.

Description

technical field [0001] The invention relates to a special polymer material, in particular to a transparent back adhesive for double-sided color-developing anodized aluminum hot stamping foil with high transparency and good cutting performance without adding fumed silica powder during use. Background technique [0002] Double-sided color-developing anodized aluminum hot stamping foil is one of the anodized aluminum hot stamping foils that can display different (or the same) colors on the front and back of the pattern after hot stamping. It is widely used in hot stamping on the surface of various transparent substrates. The color effect of the hot stamping pattern enhances the aesthetics. However, due to the limitations of the production process and technology of the conventional anodized hot stamping foil adhesive, the transparency of the adhesive material is relatively biased. During the use process, fumed silica powder needs to be added, so that the color layer on the rever...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J161/14C09J161/20C09J11/08C09J11/06
Inventor 周晋林雪峰沈丽娟
Owner ZHEJIANG HENGFENG PACKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap