Visible light responded photocatalyst LiBGe3O8 and preparation method thereof

A photocatalyst, visible light technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problems of limited types of photocatalysts, low light conversion efficiency, difficult synthesis, etc., and achieve visible light response frequency. The effect of wide range, high light conversion efficiency and simple preparation method

Inactive Publication Date: 2016-10-12
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, niobate photocatalyst Pb 3 Nb 4 o 13 、BiNbO 4 and Bi 2 MbO 7 (M=Al, Ga, In, Y, rare earth elements and Fe) etc. and niobium potassium composite oxide photocatalysts such as KNbO 3 , KNb 3 o 8 、K 4 Nb 6 o 17 and K 6 Nb 10.6 o 30 have good photocatalytic performance, but their intrinsic photocatalytic effect is weak or inactive in the visible light range.
[0005] Although photocatalysis research has been carried out for several years, most of the exploration and development of visible light-responsive photocatalysts are based on experience summaries obtained through a large number of experiments. Predict its photocatalytic performance in nature, so the types of photocatalysts with visible light response reported are still very limited, and there are problems such as low photoconversion efficiency, difficult synthesis, poor stability and narrow spectral response range, research and development of new preparations High-efficiency photocatalysts with simple methods and broad-band visible light response are difficult problems that scientists in the field have been eager to solve but have always been difficult to achieve, which largely limits the wide application and development of photocatalysts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) The analytically pure chemical raw material Li 2 CO 3 , B 2 o 3 and GeO 2 powder of LiBGe 3 o 8 The composition weighs the ingredients.

[0019] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0020] (3) Pre-fire the uniformly mixed powder in step (2) at 950°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then pulverize it with a ball mill to make the average particle diameter smaller than 2 μm, and then LiBGe is obtained 3 o 8 powder.

[0021] The prepared photocatalyst has a methyl orange removal rate of 97.7% in 60 minutes under the irradiation of visible light with a wavelength greater than 420nm.

Embodiment 2

[0023] (1) The analytically pure chemical raw material Li 2 CO 3 , B 2 o 3 and GeO 2 powder of LiBGe 3 o 8 The composition weighs the ingredients.

[0024] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0025] (3) Pre-fire the uniformly mixed powder in step (2) at 980°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then pulverize it through a ball mill to make the average particle diameter smaller than 2 μm, and then LiBGe is obtained 3 o 8 powder.

[0026] The prepared photocatalyst has a methyl orange removal rate of 98.9% in 60 minutes under the irradiation of visible light with a wavelength greater than 420nm.

Embodiment 3

[0028] (1) The analytically pure chemical raw material Li 2 CO 3 , B 2 o 3 and GeO 2 powder of LiBGe 3 o 8 The composition weighs the ingredients.

[0029] (2) Mix the raw materials prepared in step (1), put them into a ball mill jar, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0030] (3) Pre-fire the uniformly mixed powder in step (2) at 1000°C, keep it warm for 6 hours, cool it down to room temperature naturally, and then pulverize it with a ball mill to make the average particle diameter smaller than 2 μm, and then LiBGe is obtained 3 o 8 powder.

[0031] The prepared photocatalyst has a methyl orange removal rate of 98.5% in 60 minutes under the irradiation of visible light with a wavelength greater than 420nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a broadband and efficient visible light responded photocatalyst LiBGe3O8 and a preparation method thereof. The chemical formula of the photocatalyst is LiBGe3O8. The invention further discloses the preparation method of the material. The obtained photocatalyst has the advantages of wide spectral response range, high light conversion efficiency and good stability and the like. The photocatalyst has the effects of decomposing harmful chemical substances and chemical organic matters and sterilizing under the irradiation of visible light; and furthermore, the preparation method is simple, low in synthesis temperature, low in cost and suitable for industrial production and application.

Description

technical field [0001] The invention relates to a photocatalyst LiBGe responsive to visible light 3 o 8 The invention and a preparation method thereof belong to the field of inorganic photocatalytic materials. Background technique [0002] With the development of social economy, people pay more and more attention to energy and ecological environment. Solving the problems of energy shortage and environmental pollution is an urgent need to achieve sustainable development, improve people's quality of life and ensure national security. [0003] Since the late 1970s, people have proposed the use of photocatalysts to decompose organic substances such as pesticides and odorous substances in water and the atmosphere, and self-cleaning of solid surfaces coated with photocatalysts. The principle of photocatalytic reaction is that after the photocatalyst absorbs photons higher than its bandgap energy, holes and electrons are generated, and these holes and electrons undergo oxidation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/14B01J35/02
CPCB01J23/14B01J35/40B01J35/39
Inventor 段炼方亮苏和平
Owner GUILIN UNIVERSITY OF TECHNOLOGY