Visible light responsive photocatalyst Li2Fe4Si3O13 and method for preparing same

A photocatalyst and visible light technology, which is applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problems of limited photocatalyst types, low light conversion efficiency, and difficult synthesis, and achieve visible light response frequency The effect of wide range, high photoconversion efficiency and simple preparation method

Inactive Publication Date: 2016-10-12
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, niobate photocatalyst Pb 3 Nb 4 o 13 、BiNbO 4 and Bi 2 MbO 7 (M=Al, Ga, In, Y, rare earth elements and Fe) etc. and niobium potassium composite oxide photocatalysts such as KNbO 3 , KNb 3 o 8 、K 4 Nb 6 o 17 and K 6 Nb 10.6 o 30 have good photocatalytic performance, but their intrinsic photocatalytic effect is weak or inactive in the visible light range.
[0005] Although photocatalysis research has been carried out for several years, most of the exploration and development of visible light-responsive photocatalysts are based on experience summaries obtained through a large number of experiments. Predict its photocatalytic performance in nature, so the types of photocatalysts with visible light response reported are still very limited, and there are problems such as low photoconversion efficiency, difficult synthesis, poor stability and narrow spectral response range, research and development of new preparations High-efficiency photocatalysts with simple methods and broad-band visible light response are difficult problems that scientists in the field have been eager to solve but have always been difficult to achieve, which largely limits the wide application and development of photocatalysts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Analyze pure chemical raw material Li 2 CO 3 , Fe 2 O 3 And SiO 2 Powder press Li 2 Fe 4 Si 3 O 13 The composition of the weighing ingredients.

[0019] (2) Mix the raw materials prepared in step (1), put them into a ball mill tank, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0020] (3) Pre-fire the uniformly mixed powder in step (2) at 1200°C, keep it for 6 hours, cool it naturally to room temperature, and then pulverize it by a ball mill to reduce the average particle diameter to less than 2μm to obtain Li 2 Fe 4 Si 3 O 13 powder.

[0021] The prepared photocatalyst has a removal rate of 97.5% for methyl orange in 60 minutes under the irradiation of visible light with a wavelength greater than 420nm.

Embodiment 2

[0023] (1) Analyze pure chemical raw material Li 2 CO 3 , Fe 2 O 3 And SiO 2 Powder press Li 2 Fe 4 Si 3 O 13 The composition of the weighing ingredients.

[0024] (2) Mix the raw materials prepared in step (1), put them into a ball mill tank, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0025] (3) Pre-fire the uniformly mixed powder in step (2) at 1230°C, keep it for 6 hours, cool it naturally to room temperature, and then pulverize it by a ball mill to reduce the average particle diameter to less than 2μm, and then Li 2 Fe 4 Si 3 O 13 powder.

[0026] The prepared photocatalyst, under visible light with a wavelength greater than 420nm, the removal rate of methyl orange reached 99.1% in 60 minutes.

Embodiment 3

[0028] (1) Analyze pure chemical raw material Li 2 CO 3 , Fe 2 O 3 And SiO 2 Powder press Li 2 Fe 4 Si 3 O 13 The composition of the weighing ingredients.

[0029] (2) Mix the raw materials prepared in step (1), put them into a ball mill tank, add zirconia balls and absolute ethanol, ball mill for 8 hours, mix and grind, take out and dry, and pass through a 200-mesh sieve.

[0030] (3) Pre-fire the uniformly mixed powder in step (2) at 1250°C, keep it for 6 hours, cool it naturally to room temperature, and then pulverize it by a ball mill to make the average particle diameter smaller, less than 2μm, to obtain Li 2 Fe 4 Si 3 O 13 powder.

[0031] The prepared photocatalyst, under visible light with a wavelength greater than 420nm, the removal rate of methyl orange reached 98.4% in 60 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a broadband efficient visible light responsive photocatalyst Li2Fe4Si3O13 and a method for preparing the same. A chemical composition formula of the visible light responsive photocatalyst is Li2Fe4Si3O13. The visible light responsive photocatalyst and the method have the advantages that the visible light responsive photocatalyst features wide spectral response range, high light conversion efficiency, good stability and the like, and harmful chemical substance and organic biomass decomposition and sterilization effects can be realized by the visible light responsive photocatalyst under visible light illumination conditions; the method is simple and is low in synthesis temperature and cost and suitable for industrial production and application.

Description

Technical field [0001] The invention relates to a visible light-responsive photocatalyst Li 2 Fe 4 Si 3 O 13 The preparation method thereof belongs to the field of inorganic photocatalytic materials. Background technique [0002] With the development of social economy, people are paying more and more attention to energy and ecological environment. Solving energy shortage and environmental pollution is an urgent need to achieve sustainable development, improve people's quality of life, and ensure national security. [0003] From the late 1970s, people proposed the use of photocatalysts to decompose organics such as pesticides and malodorous substances in the water and the atmosphere, and self-cleaning of solid surfaces coated with photocatalysts. The principle of the photocatalytic reaction is that the photocatalyst generates holes and electrons after absorbing photons higher than its band gap energy. These holes and electrons undergo oxidation and reduction reactions respectively t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/78B01J35/02B01J35/00
CPCB01J23/78B01J35/40B01J35/39
Inventor 相怀成段炼陈爽
Owner GUILIN UNIVERSITY OF TECHNOLOGY