High-imitation-degree ivory carving and manufacturing process

A manufacturing process, ivory carving technology, which is applied in the field of high imitation ivory carving handicrafts, and can solve the problems such as rare ivory carving handicrafts

Inactive Publication Date: 2016-11-09
叶安生
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Among all kinds of handicrafts, ivory carvings are high-end works of art, and its raw materials are strictly prohibited from trading in the world. Real ivory materials are extremely rare, so ivory carving handicrafts on the market are rare. This is indeed what people appreciate in this art. regret

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 100 parts of resin, 4 parts of cobalt naphthenate solution, 1 part of cyclohexanone peroxide, 10 parts of refractory clay, and 15 parts of release agent.

[0027] Its preparation process includes the following process steps;

[0028] Preparation of release agent: Add polyvinyl alcohol to 1000-1200 parts of hot water, heat it while stirring until it is completely dissolved, then let it cool down to 60-70°C, slowly add alcohol dropwise while stirring, after the alcohol is added Then lower the temperature to below 60°C, then slowly add acetone under stirring, and filter with gauze after the dropwise addition is completed.

[0029] Apply a release agent to the inner surface of the mold;

[0030] Weigh the resin, curing agent, refractory clay, talcum powder and accelerator by mass parts and add them to mix evenly, and cast in the mold coated with the release agent;

[0031] The temperature for heating and curing and curing and molding is 30°C-35°C. The time is 10 hours, s...

Embodiment 2

[0033] 100 parts of resin, 6 parts of cobalt naphthenate solution, 2 parts of cyclohexanone peroxide, 20 parts of refractory clay, and 18 parts of release agent.

[0034] Its preparation process includes the following steps;

[0035] Make release agent; add polyvinyl alcohol to 1000-1200 parts of hot water, heat it while stirring until it is completely dissolved, then let it cool down to 10-20°C, slowly add alcohol dropwise while stirring, after the alcohol is added Then lower the temperature to below 20°C, then slowly add acetone under stirring, and filter with gauze after the dropwise addition is completed.

[0036] Apply a release agent to the inner surface of the mold;

[0037] Calculate the resin, curing agent, refractory clay, talcum powder and accelerator according to the parts by mass and mix them evenly, and cast in the mold coated with the release agent;

[0038] Heating and curing, the temperature of curing and molding is 30°C-35°C, and the time is 8 hours. After ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-imitation-degree ivory carving and a handcraft article. The handcraft article comprises 100 parts of resin, 4-6 parts of accelerant, 1-4 parts of curing agent, 10-35 parts of refractory clay, 15-20 parts of release agent and 10-20 parts of talcum powder. A manufacturing process of the handcraft article comprises the steps that firstly, the release agent is prepared; secondly, the inner surface of a mold is coated with the release agent; thirdly, the resin, the curing agent, the refractory clay and the accelerant are fetched through weighing according to the mass number and are evenly mixed, and the mixture is smeared in the mold coated with the release agent; and fourthly, curing molding is conducted, and then the high-imitation-degree ivory carving handcraft article is obtained. The handcraft article manufactured according to the manufacturing process is low in cost, simple in production process, short in production cycle, high in yield, high in artistic ornamental value, capable of achieving mass production and quite good in development prospect.

Description

technical field [0001] The invention is a high imitation ivory carving handicraft, in particular to a high imitation ivory carving and a manufacturing process. Background technique [0002] Among all kinds of handicrafts, ivory carvings are high-end works of art, and its raw materials are strictly prohibited from trading in the world. Real ivory materials are extremely rare, so ivory carving handicrafts on the market are rare. This is indeed what people appreciate in this art. regret. Contents of the invention [0003] In order to solve the above problems, the technical problem to be solved by the present invention is to provide a high imitation ivory carving and its manufacturing process. The handicrafts obtained through this process are low in cost, short in production cycle, high in artistry, and can be produced on a large scale. There are development prospects. [0004] The technical scheme adopted in the present invention is: a kind of high imitation ivory carving a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine