Preparing method of anodic oxidation die-casting aluminum alloy

A casting aluminum alloy and anodizing technology, which is applied in the field of aluminum alloy, can solve the problems that die-casting aluminum alloy cannot be anodized, and achieve good anodizing effect, excellent processing characteristics and die-casting characteristics, and good corrosion resistance.

Active Publication Date: 2016-12-07
GUANGZHOU ZHIYUAN ALLOY PROD CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem solved by the present invention is to overcome the disadvantage that the existing die-casting aluminum alloys cannot be anodized, and provide a method for preparing anodized die-casting aluminum alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The following introduces the preparation method of the anodizable die-casting aluminum alloy of the present invention, comprising the following steps:

[0020] (1) Proportioning the ingredients, wherein the content of silicon is less than or equal to 0.6%, the content of iron is 0.8%-1.8%, the content of copper is less than or equal to 1%, the content of manganese is 1.7%-3.3%, magnesium The content of zinc is less than or equal to 0.7%, the content of zinc is less than or equal to 3.5%, the content of lead is less than or equal to 0.1%, the content of tin is less than or equal to 0.2%, and the content of cadmium is less than or equal to 0.01%. is a ratio calculated by weight;

[0021] (2) Clean and remove impurities in the furnace, put aluminum ingots into the furnace for melting, and when the molten metal is heated to 880°C-900°C, put in iron and manganese agents;

[0022] (3) Stir the molten metal multiple times, and leave it to stand after each stirring;

[0023] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing method of an anodic oxidation die-casting aluminum alloy. The preparing method comprises following steps: an aluminum ingot is put into a smelting furnace to be smelted, and when the temperature rises to 880 DEG C to 900 DEG C, an iron agent and a manganese agent are put into the smelting furnace; molten metal is repeatedly stirred, and after stirring each time, standing is carried out; manganese and zinc are put into the molten metal to be smelted, and the molten metal is stirred; when the temperature of molten alloy ranges from 780 DEG C to 800 DEG C, a refining agent is added for refining and slag removal; after sufficient stirring, a sample is taken out to be subject to the test; nitrogen is led into the molten metal to achieve gas removal; if the tested component is within the set range, an alterant is added into the molten metal, and stirring and standing are carried out; pouring is carried out, and during pouring, the temperature of the molten metal is kept at 780 DEG C to 800 DEG C. The preparing method of the anodic oxidation die-casting aluminum alloy is provided and solves the technical problem that an existing die-casting aluminum alloy cannot be subject to anodic oxidation.

Description

technical field [0001] The invention relates to the field of aluminum alloys. Specifically, it is a preparation method of die-cast aluminum alloy capable of anodic oxidation. Background technique [0002] Aluminum alloy is a metal material widely used in various fields. In order to make aluminum alloy more corrosion-resistant and to color aluminum alloy parts, aluminum alloy is usually placed in an electrolyte for anodic oxidation, thereby forming an oxide film on its surface , to protect the aluminum alloy and improve the hardness of the aluminum alloy. However, commonly used die-casting alloys such as aluminum-silicon alloys, aluminum-copper alloys, and aluminum-magnesium alloys cannot be anodized and colored. In die-casting aluminum alloys, usually, the content of silicon is as high as 6%-12%, and the content of copper is also high. A high content of silicon will make the oxide film gray, and copper will make the oxide film red, and will damage the quality of the elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/02C22C21/00C22C21/10
CPCC22C1/026C22C21/00C22C21/10
Inventor 李新豪陈苏坚李升李旭涛王永科
Owner GUANGZHOU ZHIYUAN ALLOY PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap