Manufacturing technology of coated decoration board

A decorative board and production process technology, applied in the field of building boards, can solve the problems of arching, unsatisfactory waterproof effect, low board service life, etc., and achieve the effects of mellow texture, short cycle and simple process

Inactive Publication Date: 2017-02-01
JIANGSU JIFU NEW MATERIAL
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the use of composite panels, there is often serious arching when laying a large area, the waterproof effect is not ideal, and the service life of the panels is low. large-scale standardized production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing technology of coated decoration board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The manufacturing process of the clad decorative plate in this embodiment mainly produces a clad decorative plate with a thickness ≤ 50mm, and the specific steps are as follows:

[0028] S0. Base material pretreatment: carry out dust blowing treatment and deburring treatment on the surface of the base material, and the base material should be smooth without barbs when directly touched by hand.

[0029] S1. Loading: Stack the substrates in order. The substrates can be one or more of density boards, fireproof boards, particle boards and blockboards, and they are bonded with PUR glue.

[0030] S2. Feeding: Send the combined base material into the press through the rubber roller through the manipulator.

[0031] S3. Centering: The base material is fixed at the center of the press template by the centering device.

[0032] S4. Pressing: raise the temperature of the press to 100°C, the pressure to 12Mpa, and continue pressing for 1 minute.

[0033] S5. Saw board: send the l...

Embodiment 2

[0039] The manufacturing process of the clad decorative plate of the present embodiment mainly produces a clad decorative plate with a thickness of preferably 50mm-80mm, and the specific steps are as follows:

[0040] S0. Base material pretreatment: carry out dust blowing treatment and burr removal treatment on the surface of the base material. The base material should be smooth and free of barbs when directly touched by hand.

[0041] S1. Loading: Stack the substrates in order. The substrates can be one or more of density boards, fireproof boards, particle boards and blockboards, and they are bonded with PUR glue.

[0042] S2. Feeding: Send the combined base material into the press through the rubber roller through the manipulator.

[0043] S3. Centering: The base material is fixed at the center of the press template by the centering device.

[0044] S4. Pressing: raise the temperature of the press to 120°C, the pressure to 15Mpa, and continue pressing for 1 minute.

[0045...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of coated board machining, in particular to a manufacturing technology of a coated decoration board. The coated decoration board comprises a base material and a decoration layer; the flows of the manufacturing technology of the coated decoration board comprise loading, feeding, centering, pressure attaching, board sawing, chamfering, sanding, coating and discharging; according to the manufacturing technology of the coated decoration board, the environment is a good-ventilation workshop where the room temperature ranges from 15 DEG C to 35 DEG C, and the relative humidity ranges from 55% to 65%; the full-automatic assembly line is adopted in the manufacturing technology of the coated decoration board, the working procedure is simple, the period is short, the efficiency is high, the surface of the board does not need to be sealed by a sealing strip, the technology is suitable for large-scale standard production, and the produced coated decoration board has the beneficial effects of being good in waterproof performance, high in whole sense, free of arching during large-area paving, uniform in tonality and mellow in character.

Description

technical field [0001] The invention relates to the field of building boards, in particular to a manufacturing process for clad decorative boards. Background technique [0002] As the number of trees on the earth decreases day by day, people pay more and more attention to protecting forests and reducing deforestation. At present, more and more composite panels have appeared on the market to replace the original solid wood panels. However, during the use of composite panels, there is often serious arching when laying a large area, the waterproof effect is not ideal, and the service life of the panels is low. Large-scale standardized production. Contents of the invention [0003] In order to solve the above problems, the present invention provides a manufacturing process for clad decorative panels, specifically as follows: [0004] A manufacturing process of a coated decorative board, the coated decorative board includes a base material and a decorative layer; the environ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27M3/00E04F13/077
CPCB27M3/00B27M3/0086E04F13/0871E04F13/10
Inventor 葛亚
Owner JIANGSU JIFU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com