A kind of cordierite honeycomb ceramic carrier with full oxide as raw material and preparation method thereof

A cordierite honeycomb, ceramic carrier technology, applied in ceramic products, other household appliances, household appliances, etc., can solve the problems of reducing the thermal expansion coefficient, difficult extrusion molding, mold wear, etc., to reduce the thermal expansion coefficient, and the shape is easy to control. , the effect of increasing the regeneration temperature

Active Publication Date: 2019-05-21
SHANDONG AOFU ENVIRONMENTAL PROTECTION SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN104030720B discloses a cordierite honeycomb ceramic carrier with zero firing shrinkage and a preparation method thereof. In the method, the main raw materials are composed of flaky kaolin, flaky talcum powder, flaky alumina powder, magnesia powder, and silicon oxide powder. Although it is revealed that the directional arrangement of flaky alumina can reduce the coefficient of thermal expansion, the core is still oriented arrangement of flaky talc and kaolin to reduce the coefficient of thermal expansion, and the relationship between the diameter-thickness ratio of flaky alumina and the thermal expansion coefficient is not separately reflected.
However, when the raw materials are all oxides, there are some difficulties in the production of cordierite honeycomb ceramics, for example: ① lack of kaolin and talc ingredients, all oxide raw materials are barren materials, mud plasticity is poor, and extrusion molding is difficult; ② full Oxide raw materials have high hardness, and the particles have edges and corners, which will cause severe wear and tear on mud refining, extrusion equipment, and molds; ③The reactivity of all oxide raw materials is low, which will cause an increase in thermal expansion coefficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cordierite honeycomb ceramic carrier with full oxide as raw material and preparation method thereof
  • A kind of cordierite honeycomb ceramic carrier with full oxide as raw material and preparation method thereof
  • A kind of cordierite honeycomb ceramic carrier with full oxide as raw material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1. Flaky alumina with an aspect ratio of 15:1, D50=20μm-30μm, active magnesia with D50=0.2μm-0.6μm, fumed silica with D50=4μm-6μm As raw materials, their contents are: 35.8% of flake alumina, 13.5% of active magnesium oxide, and 50.7% of fumed silica.

[0053] 2. Weigh each raw material according to the above content, then add methyl cellulose with 8% of the total mass of raw materials, fully dry mix, and then add silicone polyether copolymer with 1.0% of the total mass of raw materials (such as Dow Corning’s DC series) 1. Soybean oil of 1% of the total mass of raw materials and water of 32% of the total mass of raw materials are kneaded, vacuum-soiled, and stale at room temperature for 24 hours after the kneading;

[0054] 3. After aging, extrude the mud material to obtain a ceramic carrier green body with a size of Φ330.2×152.4mm and a wall thickness of 4mil. Dry the ceramic carrier green body, and then heat it up to 1425-1430°C for 100-120h for firing , and then kee...

Embodiment 2

[0056] The cordierite honeycomb ceramic carrier was prepared according to the method of Example 1, except that the content of the raw materials was: 32% of flake alumina, 15% of active magnesium oxide, and 53% of fumed silica.

Embodiment 3

[0058] The cordierite honeycomb ceramic carrier was prepared according to the method of Example 1, except that the content of the raw materials was: 38% of flake alumina, 12% of active magnesium oxide, and 50% of fumed silica.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cordierite honeycomb ceramic carrier using complete oxides as a raw materials and a preparation method thereof. The cordierite honeycomb ceramic carrier comprises 32-38% of alumina, 12-15% of active magnesia and 47-54% of silica dioxide. The raw materials including oxides are chemical products and have wide available sources. The morphology of the raw materials is easy to control, and the materials ,can achieve a big diameter-to-thickness ratio. The inventions has the advantages of being simple in the preparation method, easy to implement, high in softening temperature, high in pass rate in the extrusion and baking processes. The cordierite mainly uses alumina as a template to grow, so it is prone to achieving the directional array of the cordierite. The acquired ceramic carrier has a low coefficient of thermal expansion.

Description

technical field [0001] The invention relates to a cordierite honeycomb ceramic carrier using total oxide as a raw material and a preparation method thereof, belonging to the technical field of catalyst carriers. Background technique [0002] The cordierite honeycomb ceramic carrier is a catalyst carrier for gaseous pollution emission post-treatment technology of internal combustion engines, such as: SCR carrier, TWC carrier, DOC carrier, DPF, GPF, etc. With the rapid tightening of emission regulations on motor vehicle exhaust pollutants and the rapid tightening of motor vehicle economic regulations, the wall thickness of the honeycomb ceramic carrier must be reduced to less than 5mil to obtain a larger surface area for catalyst coating and lower flow resistance. As the wall thickness decreases, the thermal shock performance also decreases, and the requirements for the thermal expansion coefficient (CTE) of the cordierite honeycomb ceramic carrier are higher, and the CTE is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00C04B35/195
CPCC04B35/195C04B38/0006C04B2235/3206C04B2235/3217C04B2235/3418C04B2235/9607
Inventor 黄妃慧刘洪月潘吉庆李民
Owner SHANDONG AOFU ENVIRONMENTAL PROTECTION SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products